Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 9American Society of Mechanical Engineers, 1990 - Arctic regions |
From inside the book
Results 1-3 of 59
Page 627
... corrosion currents were obtained in the sour solution as compared to the base solution . It appears that variations in the carbon content did not significantly influence the corrosion current density . For low residual steels alloyed ...
... corrosion currents were obtained in the sour solution as compared to the base solution . It appears that variations in the carbon content did not significantly influence the corrosion current density . For low residual steels alloyed ...
Page 630
... corrosion of carbon steel in sour gas environments : Effect of H2S / CO2 / CH4 / C3H8 mixtures " , Corrosion . Vol . 42 , No.7 , 1986 , p . 398 2. Adams , W.L. , and Lindley , W.A. , " Corrosion inhibition in H2S containing brine ...
... corrosion of carbon steel in sour gas environments : Effect of H2S / CO2 / CH4 / C3H8 mixtures " , Corrosion . Vol . 42 , No.7 , 1986 , p . 398 2. Adams , W.L. , and Lindley , W.A. , " Corrosion inhibition in H2S containing brine ...
Page 643
... corrosion in Figure 10. Unfortunately , only deposit G meets the toughness criterion of 40J @ -60 ° C . It was estimated that acceptable corrosion characteristics could be obtained without sacrificing the toughness target by a deposit ...
... corrosion in Figure 10. Unfortunately , only deposit G meets the toughness criterion of 40J @ -60 ° C . It was estimated that acceptable corrosion characteristics could be obtained without sacrificing the toughness target by a deposit ...
Contents
WELDING TECHNOLOGY | 387 |
PROPERTIES OF WELDMENT | 394 |
Progress in the Use of Metal Powder Additions for the Welding of Offshore Structures | 399 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
acicular ferrite alloy analysis application austenite bainite base metal carbon equivalent carbon steels cathodic protection Charpy composition corrosion crack tip critical CTOD CTOD tests CTOD values cycle defects distribution effect electrode equation evaluation experimental fabrication fatigue crack ferrite fracture mechanics fracture toughness GC HAZ GMAW grain HAZ toughness heat input HSLA Steels hyperbaric inclusions increase inspection interface J-Integral kJ/mm load lower bound estimates material measured mechanical properties method microstructure node notch obtained offshore structures overmatching parameters performance pipe powder ratio S-N curves sample shows simulation SMAW specimens stainless steel welding strain stress range submerged arc welding surface Table technique tensile panels Test Temperature TMCP steels tubular joints twin-wire ultrasonic underwater underwater welding Weibull Weibull distribution weld deposit weld metal weldability welded joints welding procedures welding process weldments wire yield strength zone