... distribution with constant shape parameter . The relation between the mean CTOD and the LBZ size is deduced from the weakest link model assuming the CTOD distribution can represented by the Weibull distribution ( Satoh et al . , 1985 ) ...
... distribution with constant shape parameter . The relation between the mean CTOD and the LBZ size is deduced from the weakest link model assuming the CTOD distribution can represented by the Weibull distribution ( Satoh et al . , 1985 ) ...
Page 571
... distribution was approximately symmetric ( Figure 5a ) , the ranges of all three lower bound estimates converged to the true lower bound as the sample size increased . However , when a skewed right distribution was sampled ( Figure 5b ) ...
... distribution was approximately symmetric ( Figure 5a ) , the ranges of all three lower bound estimates converged to the true lower bound as the sample size increased . However , when a skewed right distribution was sampled ( Figure 5b ) ...
Page 573
... Distribution No. 1 Probability 0.16 -30 % ( a ) -40 % 0 % 2.5 % 0.12 -10 % Distribution No. 1 -20 % -30 % - ( b ) -40 % 0 % 2.6 % -10 % 2 3 0.08 -20 % -30 % -40 % ( c )。 Distribution No. 0.04 1 2 3 4 Figure 8 : 10 16 20 26 30 36 0.00 ...
... Distribution No. 1 Probability 0.16 -30 % ( a ) -40 % 0 % 2.5 % 0.12 -10 % Distribution No. 1 -20 % -30 % - ( b ) -40 % 0 % 2.6 % -10 % 2 3 0.08 -20 % -30 % -40 % ( c )。 Distribution No. 0.04 1 2 3 4 Figure 8 : 10 16 20 26 30 36 0.00 ...
Contents
WELDING TECHNOLOGY | 387 |
PROPERTIES OF WELDMENT | 394 |
Progress in the Use of Metal Powder Additions for the Welding of Offshore Structures | 399 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
acicular ferrite alloy analysis application austenite bainite base metal carbon equivalent carbon steels cathodic protection Charpy composition corrosion crack tip critical CTOD CTOD tests CTOD values cycle defects distribution effect electrode equation evaluation experimental fabrication fatigue crack ferrite fracture mechanics fracture toughness GC HAZ GMAW grain HAZ toughness heat input HSLA Steels hyperbaric inclusions increase inspection interface J-Integral kJ/mm load lower bound estimates material measured mechanical properties method microstructure node notch obtained offshore structures overmatching parameters performance pipe powder ratio S-N curves sample shows simulation SMAW specimens stainless steel welding strain stress range submerged arc welding surface Table technique tensile panels Test Temperature TMCP steels tubular joints twin-wire ultrasonic underwater underwater welding Weibull Weibull distribution weld deposit weld metal weldability welded joints welding procedures welding process weldments wire yield strength zone