... inclusions would be when the maximum in size distribution is greater than the Zener particle diameter . This condition will promote larger prior austenite grains because inclusions of size larger than the Zener diameter will not hinder ...
... inclusions would be when the maximum in size distribution is greater than the Zener particle diameter . This condition will promote larger prior austenite grains because inclusions of size larger than the Zener diameter will not hinder ...
Page 527
Percent of Total Inclusions Classed 10 Inclusion Analysis The majority class of inclusions contained 25 % to 35 % of the total number of inclusions and was generally found to be in the 0.2 to 0.4 μm size range . Table 4 gives a summary ...
Percent of Total Inclusions Classed 10 Inclusion Analysis The majority class of inclusions contained 25 % to 35 % of the total number of inclusions and was generally found to be in the 0.2 to 0.4 μm size range . Table 4 gives a summary ...
Page 530
... inclusions ( Judson and McKeown , 1982 ) in combination with overall lower inclusion levels . CONCLUSIONS Welds E ... inclusions ( > 0.6 μm ) situated in grain boundary ferrite of as - deposited microstructures . The initiating ...
... inclusions ( Judson and McKeown , 1982 ) in combination with overall lower inclusion levels . CONCLUSIONS Welds E ... inclusions ( > 0.6 μm ) situated in grain boundary ferrite of as - deposited microstructures . The initiating ...
Contents
WELDING TECHNOLOGY | 387 |
PROPERTIES OF WELDMENT | 394 |
Progress in the Use of Metal Powder Additions for the Welding of Offshore Structures | 399 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
acicular ferrite alloy analysis application austenite bainite base metal carbon equivalent carbon steels cathodic protection Charpy composition corrosion crack tip critical CTOD CTOD tests CTOD values cycle defects distribution effect electrode equation evaluation experimental fabrication fatigue crack ferrite fracture mechanics fracture toughness GC HAZ GMAW grain HAZ toughness heat input HSLA Steels hyperbaric inclusions increase inspection interface J-Integral kJ/mm load lower bound estimates material measured mechanical properties method microstructure node notch obtained offshore structures overmatching parameters performance pipe powder ratio S-N curves sample shows simulation SMAW specimens stainless steel welding strain stress range submerged arc welding surface Table technique tensile panels Test Temperature TMCP steels tubular joints twin-wire ultrasonic underwater underwater welding Weibull Weibull distribution weld deposit weld metal weldability welded joints welding procedures welding process weldments wire yield strength zone