... pipe ) . Figure 2 shows typical as - welded microstructures of HPW welds in these materials . These are characterized by defect - free weld zones with diffusive grain growth across the original weld plane , completely eliminating the ...
... pipe ) . Figure 2 shows typical as - welded microstructures of HPW welds in these materials . These are characterized by defect - free weld zones with diffusive grain growth across the original weld plane , completely eliminating the ...
Page 565
... pipe is so corroded and rough that it will not reflect the ultrasonic wave back to the transducer probe and no reliable thickness measurement can be made . The EMAT , however , can be designed using Eq . ( 3 ) so that the ultrasonic ...
... pipe is so corroded and rough that it will not reflect the ultrasonic wave back to the transducer probe and no reliable thickness measurement can be made . The EMAT , however , can be designed using Eq . ( 3 ) so that the ultrasonic ...
Page 619
... pipe . After 40 days the bottom ends of all the pipes were fitted with a PVC end cap to ensure that there was no interaction with the bare steel on the inside of the pipe . Four test pipes were prepared and partially immersed in ...
... pipe . After 40 days the bottom ends of all the pipes were fitted with a PVC end cap to ensure that there was no interaction with the bare steel on the inside of the pipe . Four test pipes were prepared and partially immersed in ...
Contents
WELDING TECHNOLOGY | 387 |
PROPERTIES OF WELDMENT | 394 |
Progress in the Use of Metal Powder Additions for the Welding of Offshore Structures | 399 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
acicular ferrite alloy analysis application austenite bainite base metal carbon equivalent carbon steels cathodic protection Charpy composition corrosion crack tip critical CTOD CTOD tests CTOD values cycle defects distribution effect electrode equation evaluation experimental fabrication fatigue crack ferrite fracture mechanics fracture toughness GC HAZ GMAW grain HAZ toughness heat input HSLA Steels hyperbaric inclusions increase inspection interface J-Integral kJ/mm load lower bound estimates material measured mechanical properties method microstructure node notch obtained offshore structures overmatching parameters performance pipe powder ratio S-N curves sample shows simulation SMAW specimens stainless steel welding strain stress range submerged arc welding surface Table technique tensile panels Test Temperature TMCP steels tubular joints twin-wire ultrasonic underwater underwater welding Weibull Weibull distribution weld deposit weld metal weldability welded joints welding procedures welding process weldments wire yield strength zone