Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 9American Society of Mechanical Engineers, 1990 - Arctic regions |
From inside the book
Results 1-3 of 84
Page 450
... plate thickness effect compared with fracture toughness of non - welded plate . In the latter case , only the mechanical factor is considered and the ratios are 1 : 1.45 : 3.94 . This reveals that in case of HAZ CTOD , the plate ...
... plate thickness effect compared with fracture toughness of non - welded plate . In the latter case , only the mechanical factor is considered and the ratios are 1 : 1.45 : 3.94 . This reveals that in case of HAZ CTOD , the plate ...
Page 490
... plate failure [ 8 ] . This potential problem illustrates that more than a few all weld metal test samples are needed to verify whether the target weld metal matching levels are achieved in fabrication welds . Higher strength weld metals ...
... plate failure [ 8 ] . This potential problem illustrates that more than a few all weld metal test samples are needed to verify whether the target weld metal matching levels are achieved in fabrication welds . Higher strength weld metals ...
Page 587
... Plates up to 50mm thick have been produced achieving yield strengths in 500 MPa and high Charpy toughness excess of -40 ° C , combined with good weldability . INTRODUCTION at BHP Steel has been supplying plate steels for the ...
... Plates up to 50mm thick have been produced achieving yield strengths in 500 MPa and high Charpy toughness excess of -40 ° C , combined with good weldability . INTRODUCTION at BHP Steel has been supplying plate steels for the ...
Contents
WELDING TECHNOLOGY | 387 |
PROPERTIES OF WELDMENT | 394 |
Progress in the Use of Metal Powder Additions for the Welding of Offshore Structures | 399 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
acicular ferrite alloy analysis application austenite bainite base metal carbon equivalent carbon steels cathodic protection Charpy composition corrosion crack tip critical CTOD CTOD tests CTOD values cycle defects distribution effect electrode equation evaluation experimental fabrication fatigue crack ferrite fracture mechanics fracture toughness GC HAZ GMAW grain HAZ toughness heat input HSLA Steels hyperbaric inclusions increase inspection interface J-Integral kJ/mm load lower bound estimates material measured mechanical properties method microstructure node notch obtained offshore structures overmatching parameters performance pipe powder ratio S-N curves sample shows simulation SMAW specimens stainless steel welding strain stress range submerged arc welding surface Table technique tensile panels Test Temperature TMCP steels tubular joints twin-wire ultrasonic underwater underwater welding Weibull Weibull distribution weld deposit weld metal weldability welded joints welding procedures welding process weldments wire yield strength zone