Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 9American Society of Mechanical Engineers, 1990 - Arctic regions |
From inside the book
Results 1-3 of 51
Page 449
... region and in about 90 % confidence for the case of the minimum 20 % CG region . If we take 0.01mm as the " low CTOD " value , specimens with the minimum 15 % CG regions give the probability of less than 40 % for low CTOD . These ...
... region and in about 90 % confidence for the case of the minimum 20 % CG region . If we take 0.01mm as the " low CTOD " value , specimens with the minimum 15 % CG regions give the probability of less than 40 % for low CTOD . These ...
Page 464
... Region Surrounding \ Region Weld Metal A Base Metal A \ Base Metal A Normal Matching Under Matching Base Metal Base Metal B Over Matching Not Used Not Used Table 5 . Weldment Yield Strength Ultimate Strength MPa percent MPa percent ...
... Region Surrounding \ Region Weld Metal A Base Metal A \ Base Metal A Normal Matching Under Matching Base Metal Base Metal B Over Matching Not Used Not Used Table 5 . Weldment Yield Strength Ultimate Strength MPa percent MPa percent ...
Page 492
... region while the applied strain will tend to concentrate in the region . Even so , the crack front may then sample potential brittle regions in softening suscep- tible steels than it would in normalized steel ( effect of crack path ...
... region while the applied strain will tend to concentrate in the region . Even so , the crack front may then sample potential brittle regions in softening suscep- tible steels than it would in normalized steel ( effect of crack path ...
Contents
WELDING TECHNOLOGY | 387 |
PROPERTIES OF WELDMENT | 394 |
Progress in the Use of Metal Powder Additions for the Welding of Offshore Structures | 399 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
acicular ferrite alloy analysis application austenite bainite base metal carbon equivalent carbon steels cathodic protection Charpy composition corrosion crack tip critical CTOD CTOD tests CTOD values cycle defects distribution effect electrode equation evaluation experimental fabrication fatigue crack ferrite fracture mechanics fracture toughness GC HAZ GMAW grain HAZ toughness heat input HSLA Steels hyperbaric inclusions increase inspection interface J-Integral kJ/mm load lower bound estimates material measured mechanical properties method microstructure node notch obtained offshore structures overmatching parameters performance pipe powder ratio S-N curves sample shows simulation SMAW specimens stainless steel welding strain stress range submerged arc welding surface Table technique tensile panels Test Temperature TMCP steels tubular joints twin-wire ultrasonic underwater underwater welding Weibull Weibull distribution weld deposit weld metal weldability welded joints welding procedures welding process weldments wire yield strength zone