Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 9American Society of Mechanical Engineers, 1990 - Arctic regions |
From inside the book
Results 1-3 of 88
Page 435
... shown in Fig.6 give the values of exponent K and constant Cof Manson - Coffin's relation ( Ɛ • NK = C , E : strain amplitude , N : number of cycles ) as shown in Table 3. Base metal of steels A and B exhibit similar behavior in low ...
... shown in Fig.6 give the values of exponent K and constant Cof Manson - Coffin's relation ( Ɛ • NK = C , E : strain amplitude , N : number of cycles ) as shown in Table 3. Base metal of steels A and B exhibit similar behavior in low ...
Page 454
... shown in Figure 3 , were notched at the weld metal and CGHAZ . The notches were prepared with the help of a small drilled hole at the centre and extended by a 0.3 mm wide spark cutting . The a / W ratios were used as 0.1 , 0.3 and 0.5 ...
... shown in Figure 3 , were notched at the weld metal and CGHAZ . The notches were prepared with the help of a small drilled hole at the centre and extended by a 0.3 mm wide spark cutting . The a / W ratios were used as 0.1 , 0.3 and 0.5 ...
Page 455
... shown in Figures 11 and 12 for weld metal and HAZ notched specimens respectively . The CMOD values were measured with the 85 clip - on gauge , mounted across the mid - crack with a gauge length of 5 mm . As indicated in Figures 11 and ...
... shown in Figures 11 and 12 for weld metal and HAZ notched specimens respectively . The CMOD values were measured with the 85 clip - on gauge , mounted across the mid - crack with a gauge length of 5 mm . As indicated in Figures 11 and ...
Contents
WELDING TECHNOLOGY | 387 |
PROPERTIES OF WELDMENT | 394 |
Progress in the Use of Metal Powder Additions for the Welding of Offshore Structures | 399 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
acicular ferrite alloy analysis application austenite bainite base metal carbon equivalent carbon steels cathodic protection Charpy composition corrosion crack tip critical CTOD CTOD tests CTOD values cycle defects distribution effect electrode equation evaluation experimental fabrication fatigue crack ferrite fracture mechanics fracture toughness GC HAZ GMAW grain HAZ toughness heat input HSLA Steels hyperbaric inclusions increase inspection interface J-Integral kJ/mm load lower bound estimates material measured mechanical properties method microstructure node notch obtained offshore structures overmatching parameters performance pipe powder ratio S-N curves sample shows simulation SMAW specimens stainless steel welding strain stress range submerged arc welding surface Table technique tensile panels Test Temperature TMCP steels tubular joints twin-wire ultrasonic underwater underwater welding Weibull Weibull distribution weld deposit weld metal weldability welded joints welding procedures welding process weldments wire yield strength zone