Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 9American Society of Mechanical Engineers, 1990 - Arctic regions |
From inside the book
Results 1-3 of 88
Page 454
... specimens were aimed to sample the CGHAZ adjacent to the straight sides of the weld beads . The CCT panels ( 12 of them ) as shown in Figure 3 , were notched at the weld metal and CGHAZ . The notches were prepared with the help of a ...
... specimens were aimed to sample the CGHAZ adjacent to the straight sides of the weld beads . The CCT panels ( 12 of them ) as shown in Figure 3 , were notched at the weld metal and CGHAZ . The notches were prepared with the help of a ...
Page 480
... specimens were prepared by putting the notch ( root ) in the GC HAZ corresponding to the straight portion of the K - groove . In each specimen , the length of the specimen was perpendicular to the welding direction and the notch was on ...
... specimens were prepared by putting the notch ( root ) in the GC HAZ corresponding to the straight portion of the K - groove . In each specimen , the length of the specimen was perpendicular to the welding direction and the notch was on ...
Page 648
... specimen with the weld in the center of the sample , welding procedures recommended by the electrode manufacturers were carefully followed . In general , in the mild steel / mild steel specimens , irrespective of the welding method ...
... specimen with the weld in the center of the sample , welding procedures recommended by the electrode manufacturers were carefully followed . In general , in the mild steel / mild steel specimens , irrespective of the welding method ...
Contents
WELDING TECHNOLOGY | 387 |
PROPERTIES OF WELDMENT | 394 |
Progress in the Use of Metal Powder Additions for the Welding of Offshore Structures | 399 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
acicular ferrite alloy analysis application austenite bainite base metal carbon equivalent carbon steels cathodic protection Charpy composition corrosion crack tip critical CTOD CTOD tests CTOD values cycle defects distribution effect electrode equation evaluation experimental fabrication fatigue crack ferrite fracture mechanics fracture toughness GC HAZ GMAW grain HAZ toughness heat input HSLA Steels hyperbaric inclusions increase inspection interface J-Integral kJ/mm load lower bound estimates material measured mechanical properties method microstructure node notch obtained offshore structures overmatching parameters performance pipe powder ratio S-N curves sample shows simulation SMAW specimens stainless steel welding strain stress range submerged arc welding surface Table technique tensile panels Test Temperature TMCP steels tubular joints twin-wire ultrasonic underwater underwater welding Weibull Weibull distribution weld deposit weld metal weldability welded joints welding procedures welding process weldments wire yield strength zone