... SAW Metals 0.04 -0.06 0.20 -0.35 0.80 -1.50 0.010 0.002 0.007 ~ 0.020 -0.010 -0.25 -0.035 0.028 -0.035 - 0.003 0.022 0.13 -0.0030 -0.022 -0.037 -0.19 for weld metal than ... SAW metal . RESULTS AND DISCUSSION Heat Cycles of the T - cross 294.
... SAW Metals 0.04 -0.06 0.20 -0.35 0.80 -1.50 0.010 0.002 0.007 ~ 0.020 -0.010 -0.25 -0.035 0.028 -0.035 - 0.003 0.022 0.13 -0.0030 -0.022 -0.037 -0.19 for weld metal than ... SAW metal . RESULTS AND DISCUSSION Heat Cycles of the T - cross 294.
Page 297
... SAW metal . The effect of heat input on the hardness of fusion line is shown in Fig . 8. There is a critical heat input which assures Hv < 248 . Although the critical heat input was about 1100J / mm for the present SAW metal with Pcm ...
... SAW metal . The effect of heat input on the hardness of fusion line is shown in Fig . 8. There is a critical heat input which assures Hv < 248 . Although the critical heat input was about 1100J / mm for the present SAW metal with Pcm ...
Page 298
residue from this as - welded SAW metal . The amount of sol . B , however , decreased rapidly down to zero when N ... SAW metal . These relations suggest that the T - cross HAZ hardness 298.
residue from this as - welded SAW metal . The amount of sol . B , however , decreased rapidly down to zero when N ... SAW metal . These relations suggest that the T - cross HAZ hardness 298.
Contents
PIPELINE DESIGN AND OPERATIONS | 1 |
PIPELINE FORCES DYNAMICS AND STABILITY I | 95 |
9 | 123 |
Copyright | |
29 other sections not shown
Other editions - View all
Common terms and phrases
amplitude analysis applied Arctic Engineering axial base metal bending Buckle length buckling bundle calculated coefficient compressor Conference on Offshore corrosion crack curvature deformation developed diameter displacement ductile effect Eighth International Conference electrodes equation explosive welding failure flaw flow rate gas turbine geometry heat horizontal hydrodynamic hydrodynamic forces hydrogen inertial installation laboratory length lift force line pipe liquid load maximum measured Mechanics and Arctic meters method monitoring natural burial Offshore Mechanics Offshore Technology Conference operation parameters predicted present pressure problem procedure ratio reheated reliability repair resistance response rockdumps sand SAW metal scour depth seabed shown in Figure simulation Snøhvit soft zone soil Sørøya sour gas span Statoil steel stress structural submarine pipelines submerged arc welding Sumer surface Table Technology temperature tion tool trench velocity vertical vibration viscometer viscosity vortex vortex shedding wave