Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3American Society of Mechanical Engineers, 2001 - Arctic regions |
From inside the book
Results 1-3 of 15
Page 193
... arrest the initiated crack . Crack tip opening displacement ( CTOD ) tests and compact crack arrest ( CCA ) tests were conducted to measure crack initiation toughness and crack arrest toughness , respectively . While CTOD tests showed a ...
... arrest the initiated crack . Crack tip opening displacement ( CTOD ) tests and compact crack arrest ( CCA ) tests were conducted to measure crack initiation toughness and crack arrest toughness , respectively . While CTOD tests showed a ...
Page 194
... Crack tip opening displacement ( CTOD ) tests and compact crack arrest ( CCA ) tests were conducted to measure crack initiation toughness and crack arrest toughness , respectively . The LBZ effects on brittle fracture resistance were ...
... Crack tip opening displacement ( CTOD ) tests and compact crack arrest ( CCA ) tests were conducted to measure crack initiation toughness and crack arrest toughness , respectively . The LBZ effects on brittle fracture resistance were ...
Page 197
... crack initiation toughness and crack arrest toughness obtained from CTOD and CCA tests , respectively . The primary results of this investigation were ; ( 1 ) Through CTOD tests using actually welded HAZ specimens , the change in crack ...
... crack initiation toughness and crack arrest toughness obtained from CTOD and CCA tests , respectively . The primary results of this investigation were ; ( 1 ) Through CTOD tests using actually welded HAZ specimens , the change in crack ...
Contents
Fatigue Capacity | 1 |
OMAE2001MAT3011 | 11 |
OMAE2001MAT3013 | 17 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied Arctic Engineering assessment axial base metal bending brittle buckling calculated CGHAZ Charpy impact Charpy impact test components compressive Conference on Offshore crack arrest crack growth criterion CTOD test cycle defined deformation developed discrete displacement distribution DQEM ductile crack initiation dynamic effect elastic equation evaluated failure fatigue cracks ferrite Figure finite element flexible pipe FPSO Fracture Mechanics fracture toughness function fusion line hot spot hull indentation linepipe loading material maximum mechanical properties Mechanics and Arctic method microstructure node notch obtained Offshore Mechanics offshore structures parameters performed pipeline predicted pressure region Rio de Janeiro riser S-N curves shown in Fig shows simulated specimens steel plates stress concentration stress intensity factor surface cracks surface layer Table temperature tensile strength thermal thickness underwater underwater welding virgin steel Weibull distribution weld metal weld toe welded joints weldment yield strength