Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3American Society of Mechanical Engineers, 2001 - Arctic regions |
From inside the book
Results 1-3 of 47
Page 105
... types of pipe materials , LN4 and HN4 , was carried out . The geometry of the
model of straight pipeline is a diameter 610mm and a thickness 14 . 7mm . Figure
19 shows the schematic deformation of buried pipeline due to lateral spreading .
... types of pipe materials , LN4 and HN4 , was carried out . The geometry of the
model of straight pipeline is a diameter 610mm and a thickness 14 . 7mm . Figure
19 shows the schematic deformation of buried pipeline due to lateral spreading .
Page 141
When welding hot - tapping saddles onto large diameter pipelines , large
variations in gap between the saddle and the pipeline surface are to be expected
. Friction Stitch Welding procedures are being developed for sleeve welds where
the ...
When welding hot - tapping saddles onto large diameter pipelines , large
variations in gap between the saddle and the pipeline surface are to be expected
. Friction Stitch Welding procedures are being developed for sleeve welds where
the ...
Page 225
ABSTRACT API X65 steel is generally used as natural gas transmission pipeline
in Korea . The welded joint has a gradient of microstructure and mechanical
properties from fusion line to the unaffected base metal . Especially , Heat
Affected ...
ABSTRACT API X65 steel is generally used as natural gas transmission pipeline
in Korea . The welded joint has a gradient of microstructure and mechanical
properties from fusion line to the unaffected base metal . Especially , Heat
Affected ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
OMAE2001MAT3010 | 1 |
OMAE2001MAT3011 | 11 |
OMAE2001MAT3013 | 17 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment bending boundary buckling calculated Charpy compared components compressive considered controlled corrosion crack crack initiation critical CTOD curve cycle defects defined deformation derivatives determined developed direction discrete displacement distribution ductile crack dynamic effect element Engineering equation estimated evaluated experiments factors failure fatigue fatigue cracks field Figure finite element flexible FPSO fracture toughness function geometry grain growth higher impact increase inspection International joints layer length loading material maximum measured mechanical metal method microstructure node notch observed obtained offshore operation parameters performed phase pipe pipeline plastic plate predicted present pressure prestrained problem procedure range region respectively riser shown shows simulated specimens standard steel strain strength stress structures surface Table technique temperature tensile thickness weight weld yield