Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3American Society of Mechanical Engineers, 2001 - Arctic regions |
From inside the book
Results 1-3 of 92
Page 87
specimens . Figure 1 gives the configuration of all of the specimens used . A smooth round - bar tensile specimens with a diameter of 6mm and four types of tensile specimens with circumferential notch which is four kinds of different ...
specimens . Figure 1 gives the configuration of all of the specimens used . A smooth round - bar tensile specimens with a diameter of 6mm and four types of tensile specimens with circumferential notch which is four kinds of different ...
Page 109
... SPECIMENS The specimens are listed in Table 2. Tension specimens , corrosion specimens , and joint specimens ( excluding rope specimens ) were fabricated using each material . 3.1 Non - ferrous metal and steel specimens The geometry of ...
... SPECIMENS The specimens are listed in Table 2. Tension specimens , corrosion specimens , and joint specimens ( excluding rope specimens ) were fabricated using each material . 3.1 Non - ferrous metal and steel specimens The geometry of ...
Page 112
... Specimens after 1 - year exposure were reclaimed as scheduled from the Miyako - jima exposure site in August 2000 and subjected to tension testing . The appearances of the specimens were similar to those observed at the 6 - month ...
... Specimens after 1 - year exposure were reclaimed as scheduled from the Miyako - jima exposure site in August 2000 and subjected to tension testing . The appearances of the specimens were similar to those observed at the 6 - month ...
Contents
Fatigue Capacity | 1 |
OMAE2001MAT3011 | 11 |
OMAE2001MAT3013 | 17 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied Arctic Engineering assessment axial base metal bending brittle buckling calculated CGHAZ Charpy impact Charpy impact test components compressive Conference on Offshore crack arrest crack growth criterion CTOD test cycle defined deformation developed discrete displacement distribution DQEM ductile crack initiation dynamic effect elastic equation evaluated failure fatigue cracks ferrite Figure finite element flexible pipe FPSO Fracture Mechanics fracture toughness function fusion line hot spot hull indentation linepipe loading material maximum mechanical properties Mechanics and Arctic method microstructure node notch obtained Offshore Mechanics offshore structures parameters performed pipeline predicted pressure region Rio de Janeiro riser S-N curves shown in Fig shows simulated specimens steel plates stress concentration stress intensity factor surface cracks surface layer Table temperature tensile strength thermal thickness underwater underwater welding virgin steel Weibull distribution weld metal weld toe welded joints weldment yield strength