Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3American Society of Mechanical Engineers, 2001 - Arctic regions |
From inside the book
Results 1-3 of 93
Page 174
... thickness Bottom surface Figure 10 Hardness distribution through plate Absorbed Energy at -40 ° C ( J ) thickness 400 아 FCAW ( as welded ) 1-1 0 : 2mm under top surface ( cap ) A : Mid thickness : 2mm over bottom surface ( root ) 300 ...
... thickness Bottom surface Figure 10 Hardness distribution through plate Absorbed Energy at -40 ° C ( J ) thickness 400 아 FCAW ( as welded ) 1-1 0 : 2mm under top surface ( cap ) A : Mid thickness : 2mm over bottom surface ( root ) 300 ...
Page 179
... thickness , cm ; d is diameter or width of structural member section in contact with ice , cm . I , fc are coefficient for pile shape and contact unevenness . ( 2 ) Schwarz Formula Schwarz formula was proposed by Schwarz , Hiayama and ...
... thickness , cm ; d is diameter or width of structural member section in contact with ice , cm . I , fc are coefficient for pile shape and contact unevenness . ( 2 ) Schwarz Formula Schwarz formula was proposed by Schwarz , Hiayama and ...
Page 196
... thickness difference between CTOD specimens and CCA specimens due to the side - grooves in CCA test specimens should be corrected because fracture toughness increases with decreasing thickness . Japanese standard WES- 3003 ( 1983 ) ...
... thickness difference between CTOD specimens and CCA specimens due to the side - grooves in CCA test specimens should be corrected because fracture toughness increases with decreasing thickness . Japanese standard WES- 3003 ( 1983 ) ...
Contents
Fatigue Capacity | 1 |
OMAE2001MAT3011 | 11 |
OMAE2001MAT3013 | 17 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied Arctic Engineering assessment axial base metal bending brittle buckling calculated CGHAZ Charpy impact Charpy impact test components compressive Conference on Offshore crack arrest crack growth criterion CTOD test cycle defined deformation developed discrete displacement distribution DQEM ductile crack initiation dynamic effect elastic equation evaluated failure fatigue cracks ferrite Figure finite element flexible pipe FPSO Fracture Mechanics fracture toughness function fusion line hot spot hull indentation linepipe loading material maximum mechanical properties Mechanics and Arctic method microstructure node notch obtained Offshore Mechanics offshore structures parameters performed pipeline predicted pressure region Rio de Janeiro riser S-N curves shown in Fig shows simulated specimens steel plates stress concentration stress intensity factor surface cracks surface layer Table temperature tensile strength thermal thickness underwater underwater welding virgin steel Weibull distribution weld metal weld toe welded joints weldment yield strength