... metal , weld metal and HAZ . Charpy impact results , as shown in Table 4 , were undertaken according to the classification society's specification and were found to satisfy the minimum requirements . Fracture toughness tests ( CTOD ) ...
... metal , weld metal and HAZ . Charpy impact results , as shown in Table 4 , were undertaken according to the classification society's specification and were found to satisfy the minimum requirements . Fracture toughness tests ( CTOD ) ...
Page 228
... and middle lines . This phenomenon was explained by the annealing heat treatment of the constant heat input from outer welding paths . Base Weld metal metal Outer line Middle line Inner line- 228 Copyright 2001 by ASME.
... and middle lines . This phenomenon was explained by the annealing heat treatment of the constant heat input from outer welding paths . Base Weld metal metal Outer line Middle line Inner line- 228 Copyright 2001 by ASME.
Page 323
weld metal at -0.4 and -2V . The LT base metal at -0.4V showed large dimples , which were typical ductile fracture mode . Also the weld metal at -0.4V appeared to have a ductile fracture mode , but the size of dimples was smaller than ...
weld metal at -0.4 and -2V . The LT base metal at -0.4V showed large dimples , which were typical ductile fracture mode . Also the weld metal at -0.4V appeared to have a ductile fracture mode , but the size of dimples was smaller than ...
Contents
Fatigue Capacity | 1 |
OMAE2001MAT3011 | 11 |
OMAE2001MAT3013 | 17 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied Arctic Engineering assessment axial base metal bending brittle buckling calculated CGHAZ Charpy impact Charpy impact test components compressive Conference on Offshore crack arrest crack growth criterion CTOD test cycle defined deformation developed discrete displacement distribution DQEM ductile crack initiation dynamic effect elastic equation evaluated failure fatigue cracks ferrite Figure finite element flexible pipe FPSO Fracture Mechanics fracture toughness function fusion line hot spot hull indentation linepipe loading material maximum mechanical properties Mechanics and Arctic method microstructure node notch obtained Offshore Mechanics offshore structures parameters performed pipeline predicted pressure region Rio de Janeiro riser S-N curves shown in Fig shows simulated specimens steel plates stress concentration stress intensity factor surface cracks surface layer Table temperature tensile strength thermal thickness underwater underwater welding virgin steel Weibull distribution weld metal weld toe welded joints weldment yield strength