Glass, Volume 26Minoru Tomozawa, R. H. Doremus Academic Press, 1977 - Glass |
From inside the book
Results 1-3 of 59
Page 139
... Table I for elemental composition . TABLE IV COMPARISON OF Mg - Si - Al - O - N PROPERTIES WITH AND WITHOUT NITROGENa Composition ( wt . % ) Sample Density Vicker's hardness number MgO SiO2 Al2O3 Si3N4 ( gm / cm3 ) T , ( ° C ) ( kg ...
... Table I for elemental composition . TABLE IV COMPARISON OF Mg - Si - Al - O - N PROPERTIES WITH AND WITHOUT NITROGENa Composition ( wt . % ) Sample Density Vicker's hardness number MgO SiO2 Al2O3 Si3N4 ( gm / cm3 ) T , ( ° C ) ( kg ...
Page 144
... Table I. Differential thermal analysis ( DTA ) and x - ray diffraction ( XRD ) analysis of specimens heated for various combinations of times and temperatures revealed extremely complex crystalli- zation behavior . The glasses were ...
... Table I. Differential thermal analysis ( DTA ) and x - ray diffraction ( XRD ) analysis of specimens heated for various combinations of times and temperatures revealed extremely complex crystalli- zation behavior . The glasses were ...
Page 145
... Table VII . The density and microhardness values are similar to those for the uncrystallized specimens presented in Table II . Because they were heated more extensively , Messier's glasses were more highly crystalline than those studied ...
... Table VII . The density and microhardness values are similar to those for the uncrystallized specimens presented in Table II . Because they were heated more extensively , Messier's glasses were more highly crystalline than those studied ...
Contents
vii | 57 |
RONALD E LOEHMAN 119 Sandia National Laboratories Albuquerque | 119 |
HeavyMetal Fluoride Glasses | 151 |
Copyright | |
3 other sections not shown
Common terms and phrases
absorption coefficient AlF3 analysis Basis for Nuclear bead seal behavior Bendow borosilicate glass bulk glasses bulk modulus CCl4 Ceram chemical composite sphere constant cooling corrosion crystalline crystallization curve dB/km devices dielectric Drexhage effects elastic electrical electron energy fibers fluorohafnate fluorozirconate glasses fused silica glass formation glass transition glass transition temperature glass-clad glass-forming region heavy-metal fluoride glasses increase interface traps ions layers leachability leaching Loehman Lucas materials measured melt metal Mitachi modulus MOSFET Moynihan nitride nitrogen Non-Cryst Nuclear Waste Nuclear Waste Management observed optical optical fibers oxide glasses oxynitride glasses Phys Poulain properties Radioactive Waste radionuclides refractive index Rekhson result sample sandwich seal Scherer seal Eq setting temperature shown in Fig silicon SiO2 SiO2 films Solids solution split ring stiffness ratio stress relaxation structural relaxation studies Subsection substrate surface Table techniques thermal thickness viscoelastic viscosity vitreous vitrification Waste Management waste-glass forms wavelength ZBLA ZBLAN ZrF4