Glass, Volume 26Minoru Tomozawa, R. H. Doremus Academic Press, 1977 - Glass |
From inside the book
Results 1-3 of 4
Page 183
... ZBLAN 55.8ZrF4-14.4BaF2-5.8LaF3-3.8AIF3-20.2NaF BZnYbT 19BaF2-27ZnF2-27YbF3-27ThF4 BZnLuT 19BaF2-27ZnF2-27LuF3-27ThF4 BZnYAT BYAT 20BaF2-29ZnF2-14.4YF3-14.4AIF3-22.2ThF4 20BaF2-29YF3-29AIF3-22ThF4 Since many glass properties are not ...
... ZBLAN 55.8ZrF4-14.4BaF2-5.8LaF3-3.8AIF3-20.2NaF BZnYbT 19BaF2-27ZnF2-27YbF3-27ThF4 BZnLuT 19BaF2-27ZnF2-27LuF3-27ThF4 BZnYAT BYAT 20BaF2-29ZnF2-14.4YF3-14.4AIF3-22.2ThF4 20BaF2-29YF3-29AIF3-22ThF4 Since many glass properties are not ...
Page 187
... ZBLAN glass has been studied by McCarthy et al . ( 1982 ) . Within this range , the conductivity - temperature curve was found to be very similar to that observed for a borosilicate glass ; values ranged from 3.7 x 10-4 W / cm K at 1.5 ...
... ZBLAN glass has been studied by McCarthy et al . ( 1982 ) . Within this range , the conductivity - temperature curve was found to be very similar to that observed for a borosilicate glass ; values ranged from 3.7 x 10-4 W / cm K at 1.5 ...
Page 193
... ZBLAN , 174 ; BZnLuT , 151 . Within a given system , the variation of a with composition can be significant . In their systematic studies of the glass - forming region in the ZrF4- BaF2 - GdF3 ternary , Takahashi et al . ( 1981 ) found ...
... ZBLAN , 174 ; BZnLuT , 151 . Within a given system , the variation of a with composition can be significant . In their systematic studies of the glass - forming region in the ZrF4- BaF2 - GdF3 ternary , Takahashi et al . ( 1981 ) found ...
Contents
vii | 57 |
RONALD E LOEHMAN 119 Sandia National Laboratories Albuquerque | 119 |
HeavyMetal Fluoride Glasses | 151 |
Copyright | |
3 other sections not shown
Common terms and phrases
absorption coefficient AlF3 analysis Basis for Nuclear bead seal behavior Bendow borosilicate glass bulk glasses bulk modulus CCl4 Ceram chemical composite sphere constant cooling corrosion crystalline crystallization curve dB/km devices dielectric Drexhage effects elastic electrical electron energy fibers fluorohafnate fluorozirconate glasses fused silica glass formation glass transition glass transition temperature glass-clad glass-forming region heavy-metal fluoride glasses increase interface traps ions layers leachability leaching Loehman Lucas materials measured melt metal Mitachi modulus MOSFET Moynihan nitride nitrogen Non-Cryst Nuclear Waste Nuclear Waste Management observed optical optical fibers oxide glasses oxynitride glasses Phys Poulain properties Radioactive Waste radionuclides refractive index Rekhson result sample sandwich seal Scherer seal Eq setting temperature shown in Fig silicon SiO2 SiO2 films Solids solution split ring stiffness ratio stress relaxation structural relaxation studies Subsection substrate surface Table techniques thermal thickness viscoelastic viscosity vitreous vitrification Waste Management waste-glass forms wavelength ZBLA ZBLAN ZrF4