Glass, Volume 26Minoru Tomozawa, R. H. Doremus Academic Press, 1977 - Glass |
From inside the book
Results 1-3 of 26
Page 77
... durability of the solidified product , as illustrated in Table IX ( Plodinec et al . , 1982 ) . Even for the many different compositions shown , waste - glass products can be readily produced with good durability . B. Chemical Durability ...
... durability of the solidified product , as illustrated in Table IX ( Plodinec et al . , 1982 ) . Even for the many different compositions shown , waste - glass products can be readily produced with good durability . B. Chemical Durability ...
Page 78
... durability SiO 2 B203 Na2O Li2O CaO MgO TiO2 ZrO2 , La203 Waste components Increases viscosity greatly ; reduces ... durability in low amounts , reduces in large amounts Reduces durability Reduces durability , but less than Na2O ...
... durability SiO 2 B203 Na2O Li2O CaO MgO TiO2 ZrO2 , La203 Waste components Increases viscosity greatly ; reduces ... durability in low amounts , reduces in large amounts Reduces durability Reduces durability , but less than Na2O ...
Page 82
... durability have long been recognized ( Morey , 1954 ; Jones , 1971 ; Eitel , 1976 ; Doremus , 1979 ; Kreidl , 1983 ) . As the ratio of oxygen to network formers such as silicon decreases , more bridging oxygens are produced and result ...
... durability have long been recognized ( Morey , 1954 ; Jones , 1971 ; Eitel , 1976 ; Doremus , 1979 ; Kreidl , 1983 ) . As the ratio of oxygen to network formers such as silicon decreases , more bridging oxygens are produced and result ...
Contents
vii | 57 |
RONALD E LOEHMAN 119 Sandia National Laboratories Albuquerque | 119 |
HeavyMetal Fluoride Glasses | 151 |
Copyright | |
3 other sections not shown
Common terms and phrases
absorption coefficient AlF3 analysis Basis for Nuclear bead seal behavior Bendow borosilicate glass bulk glasses bulk modulus CCl4 Ceram chemical composite sphere constant cooling corrosion crystalline crystallization curve dB/km devices dielectric Drexhage effects elastic electrical electron energy fibers fluorohafnate fluorozirconate glasses fused silica glass formation glass transition glass transition temperature glass-clad glass-forming region heavy-metal fluoride glasses increase interface traps ions layers leachability leaching Loehman Lucas materials measured melt metal Mitachi modulus MOSFET Moynihan nitride nitrogen Non-Cryst Nuclear Waste Nuclear Waste Management observed optical optical fibers oxide glasses oxynitride glasses Phys Poulain properties Radioactive Waste radionuclides refractive index Rekhson result sample sandwich seal Scherer seal Eq setting temperature shown in Fig silicon SiO2 SiO2 films Solids solution split ring stiffness ratio stress relaxation structural relaxation studies Subsection substrate surface Table techniques thermal thickness viscoelastic viscosity vitreous vitrification Waste Management waste-glass forms wavelength ZBLA ZBLAN ZrF4