... fluorozirconate glass via hot pressing . The chemical resistance of the glasses to corrosive fluoridating agents such as HF , F2 , and UF6 has suggested their use as containers or ... FLUORIDE GLASSES 155 of Heavy-Metal Fluoride Glasses.
... fluorozirconate glass via hot pressing . The chemical resistance of the glasses to corrosive fluoridating agents such as HF , F2 , and UF6 has suggested their use as containers or ... FLUORIDE GLASSES 155 of Heavy-Metal Fluoride Glasses.
Page 162
... glasses of composition 57ZrF4- 22 BaF2-7.7ThF4-4.2 LaF3-6.9 LiF - 3.4NaF - 1.8 PbF2-0.4 CaF2-0.6 AIF3 could be prepared as castings 1-2 cm thick and weighing 2-3 kg . Tran et al . ( 1982a ) described a series of lanthanum fluorozirconate ...
... glasses of composition 57ZrF4- 22 BaF2-7.7ThF4-4.2 LaF3-6.9 LiF - 3.4NaF - 1.8 PbF2-0.4 CaF2-0.6 AIF3 could be prepared as castings 1-2 cm thick and weighing 2-3 kg . Tran et al . ( 1982a ) described a series of lanthanum fluorozirconate ...
Page 195
... glass surface . Simmons et al . ( 1982a ) found no changes in the infrared spectra of their fluorozirconate glass samples after a 20 - hr exposure to 100 % relative humidity with conditions adjusted to avoid condensation ...
... glass surface . Simmons et al . ( 1982a ) found no changes in the infrared spectra of their fluorozirconate glass samples after a 20 - hr exposure to 100 % relative humidity with conditions adjusted to avoid condensation ...
Contents
vii | 57 |
RONALD E LOEHMAN 119 Sandia National Laboratories Albuquerque | 119 |
HeavyMetal Fluoride Glasses | 151 |
Copyright | |
3 other sections not shown
Common terms and phrases
absorption coefficient AlF3 analysis Basis for Nuclear bead seal behavior Bendow borosilicate glass bulk glasses bulk modulus CCl4 Ceram chemical composite sphere constant cooling corrosion crystalline crystallization curve dB/km devices dielectric Drexhage effects elastic electrical electron energy fibers fluorohafnate fluorozirconate glasses fused silica glass formation glass transition glass transition temperature glass-clad glass-forming region heavy-metal fluoride glasses increase interface traps ions layers leachability leaching Loehman Lucas materials measured melt metal Mitachi modulus MOSFET Moynihan nitride nitrogen Non-Cryst Nuclear Waste Nuclear Waste Management observed optical optical fibers oxide glasses oxynitride glasses Phys Poulain properties Radioactive Waste radionuclides refractive index Rekhson result sample sandwich seal Scherer seal Eq setting temperature shown in Fig silicon SiO2 SiO2 films Solids solution split ring stiffness ratio stress relaxation structural relaxation studies Subsection substrate surface Table techniques thermal thickness viscoelastic viscosity vitreous vitrification Waste Management waste-glass forms wavelength ZBLA ZBLAN ZrF4