Glass, Volume 26Minoru Tomozawa, R. H. Doremus Academic Press, 1977 - Glass |
From inside the book
Results 1-3 of 19
Page 16
... fused silica tube . Between the outer and inner walls , dry , clean N2 is flowing in order to prevent impurities from permeating to the oxidation region . The cleaned Si wafers are usually loaded vertically on fused silica carriers ...
... fused silica tube . Between the outer and inner walls , dry , clean N2 is flowing in order to prevent impurities from permeating to the oxidation region . The cleaned Si wafers are usually loaded vertically on fused silica carriers ...
Page 48
... fused silica that is found to be between 3.79 and 3.83 , depending on the type of silica measured ( Fontanella et al . , 1979 ) . For this reason , the dielectric constant of the amorphous film can be presumed to be controlled by the ...
... fused silica that is found to be between 3.79 and 3.83 , depending on the type of silica measured ( Fontanella et al . , 1979 ) . For this reason , the dielectric constant of the amorphous film can be presumed to be controlled by the ...
Page 235
... fused silica ( ~ 1.3 μm ) . The location of 20 is in good agreement with the predictions made by Nassau ( 1980 ) , although it is somewhat removed in wavelength from the anticipated loss minimum ( ~ 2.5– 3.5 μm ) . Very high information ...
... fused silica ( ~ 1.3 μm ) . The location of 20 is in good agreement with the predictions made by Nassau ( 1980 ) , although it is somewhat removed in wavelength from the anticipated loss minimum ( ~ 2.5– 3.5 μm ) . Very high information ...
Contents
vii | 57 |
RONALD E LOEHMAN 119 Sandia National Laboratories Albuquerque | 119 |
HeavyMetal Fluoride Glasses | 151 |
Copyright | |
3 other sections not shown
Common terms and phrases
absorption coefficient AlF3 analysis Basis for Nuclear bead seal behavior Bendow borosilicate glass bulk glasses bulk modulus CCl4 Ceram chemical composite sphere constant cooling corrosion crystalline crystallization curve dB/km devices dielectric Drexhage effects elastic electrical electron energy fibers fluorohafnate fluorozirconate glasses fused silica glass formation glass transition glass transition temperature glass-clad glass-forming region heavy-metal fluoride glasses increase interface traps ions layers leachability leaching Loehman Lucas materials measured melt metal Mitachi modulus MOSFET Moynihan nitride nitrogen Non-Cryst Nuclear Waste Nuclear Waste Management observed optical optical fibers oxide glasses oxynitride glasses Phys Poulain properties Radioactive Waste radionuclides refractive index Rekhson result sample sandwich seal Scherer seal Eq setting temperature shown in Fig silicon SiO2 SiO2 films Solids solution split ring stiffness ratio stress relaxation structural relaxation studies Subsection substrate surface Table techniques thermal thickness viscoelastic viscosity vitreous vitrification Waste Management waste-glass forms wavelength ZBLA ZBLAN ZrF4