Glass, Volume 26Minoru Tomozawa, R. H. Doremus Academic Press, 1977 - Glass |
From inside the book
Results 1-3 of 16
Page 137
... modulus , measured by an ultrasonic technique , showed a trend toward increasing modulus with higher nitrogen contents . Those data are summarized in Table II . Figures 10 and 11 ( Frishchat and Schrimpf , 1980 ) show that the ...
... modulus , measured by an ultrasonic technique , showed a trend toward increasing modulus with higher nitrogen contents . Those data are summarized in Table II . Figures 10 and 11 ( Frishchat and Schrimpf , 1980 ) show that the ...
Page 255
... modulus ; as t → ∞ , J2 → 1 / 3K , + 1 / 3K2 , so the bulk modulus decreases toward K1K2 / ( K1 + K2 ) . Corsaro ( 1976 ) performed such an experiment on B2O3 and showed that the bulk modulus relaxed to ~ of its initial value . Of ...
... modulus ; as t → ∞ , J2 → 1 / 3K , + 1 / 3K2 , so the bulk modulus decreases toward K1K2 / ( K1 + K2 ) . Corsaro ( 1976 ) performed such an experiment on B2O3 and showed that the bulk modulus relaxed to ~ of its initial value . Of ...
Page 313
... modulus of elastic member of composite Young's modulus of glass member of composite Young's modulus in core of composite sphere or in glass type 1 in glass - to - glass seal Young's modulus in cladding of composite sphere or in glass ...
... modulus of elastic member of composite Young's modulus of glass member of composite Young's modulus in core of composite sphere or in glass type 1 in glass - to - glass seal Young's modulus in cladding of composite sphere or in glass ...
Contents
Nuclear Waste Glasses | 57 |
Oxynitride Glasses | 119 |
HeavyMetal Fluoride Glasses | 151 |
Copyright | |
3 other sections not shown
Common terms and phrases
absorption coefficient AlF3 analysis BaF2 Basis for Nuclear bead seal behavior Bendow borosilicate glass bulk glasses CCl4 Ceram chemical cooling corrosion crystalline crystallization curve dB/km devices dielectric Drexhage effects elastic electrical electron energy fibers fluorohafnate glasses fluorozirconate glasses fused silica glass formation glass transition glass transition temperature glass-forming region heavy-metal fluoride glasses HfF4 impurities increase interface traps ions layers leaching Loehman Lucas Manabe Matecki materials measured melt metal Mitachi Miyashita Moynihan nitride nitrogen Non-Cryst Nuclear Waste Nuclear Waste Management observed optical optical fibers oxide glasses oxynitride glasses Phys prepared properties Radioactive Waste radionuclides refractive index Rekhson relaxation function sample sandwich seal scattering setting temperature shown in Fig silicon SiO2 Solids solution stiffness ratio stress relaxation structural relaxation studies Subsection substrate surface Table techniques ternary thermal ThF4 thickness viscoelastic viscosity vitreous fluorides vitrification Waste Management waste-glass forms wavelength ZBLA ZBLAN ZrF4