Glass, Volume 26Minoru Tomozawa, R. H. Doremus Academic Press, 1977 - Glass |
From inside the book
Results 1-3 of 35
Page 121
Minoru Tomozawa, R. H. Doremus. oxide portions of some oxynitride glasses ( Loehman , 1980 ) , dissolved between 0.25- and 2.5 - wt . % N2 at 1550 ° C under 1 - atm N2 . Incorporation of gaseous nitrogen was very slow and required about ...
Minoru Tomozawa, R. H. Doremus. oxide portions of some oxynitride glasses ( Loehman , 1980 ) , dissolved between 0.25- and 2.5 - wt . % N2 at 1550 ° C under 1 - atm N2 . Incorporation of gaseous nitrogen was very slow and required about ...
Page 135
... oxygen on one- fourth of the anion sites in his composition ( N / N + 0 = 0.25 ) and yielded oxynitride glasses with very high nitrogen contents . Bagaasen and Risbud ( 1983 ) synthesized and reported the properties of another class of ...
... oxygen on one- fourth of the anion sites in his composition ( N / N + 0 = 0.25 ) and yielded oxynitride glasses with very high nitrogen contents . Bagaasen and Risbud ( 1983 ) synthesized and reported the properties of another class of ...
Page 147
... oxynitride glass compositions , the calculated R ' falls between 2.16 and 2.96 , which compares with the 2.25 to 2.75 value found for many oxide glasses ( Kingery et al . , 1976 ) . The average number of bridging anions per tetrahedron ...
... oxynitride glass compositions , the calculated R ' falls between 2.16 and 2.96 , which compares with the 2.25 to 2.75 value found for many oxide glasses ( Kingery et al . , 1976 ) . The average number of bridging anions per tetrahedron ...
Contents
vii | 57 |
RONALD E LOEHMAN 119 Sandia National Laboratories Albuquerque | 119 |
HeavyMetal Fluoride Glasses | 151 |
Copyright | |
3 other sections not shown
Common terms and phrases
absorption coefficient AlF3 analysis Basis for Nuclear bead seal behavior Bendow borosilicate glass bulk glasses bulk modulus CCl4 Ceram chemical composite sphere constant cooling corrosion crystalline crystallization curve dB/km devices dielectric Drexhage effects elastic electrical electron energy fibers fluorohafnate fluorozirconate glasses fused silica glass formation glass transition glass transition temperature glass-clad glass-forming region heavy-metal fluoride glasses increase interface traps ions layers leachability leaching Loehman Lucas materials measured melt metal Mitachi modulus MOSFET Moynihan nitride nitrogen Non-Cryst Nuclear Waste Nuclear Waste Management observed optical optical fibers oxide glasses oxynitride glasses Phys Poulain properties Radioactive Waste radionuclides refractive index Rekhson result sample sandwich seal Scherer seal Eq setting temperature shown in Fig silicon SiO2 SiO2 films Solids solution split ring stiffness ratio stress relaxation structural relaxation studies Subsection substrate surface Table techniques thermal thickness viscoelastic viscosity vitreous vitrification Waste Management waste-glass forms wavelength ZBLA ZBLAN ZrF4