Glass, Volume 26Minoru Tomozawa, R. H. Doremus Academic Press, 1977 - Glass |
From inside the book
Results 1-3 of 48
Page 88
... similar to the attack in neutral solutions . For these glasses , glass dissolution is also proportional to the square root of time , and the effect of acid concentration or low pH is small . In contrast , there exists another group of ...
... similar to the attack in neutral solutions . For these glasses , glass dissolution is also proportional to the square root of time , and the effect of acid concentration or low pH is small . In contrast , there exists another group of ...
Page 144
... similar to those found for the parent glasses . There was no apparent systematic dependence of any of the electrical properties on nitrogen content , a result similar to that observed with uncrystallized material . TABLE VI PHASES IN Y ...
... similar to those found for the parent glasses . There was no apparent systematic dependence of any of the electrical properties on nitrogen content , a result similar to that observed with uncrystallized material . TABLE VI PHASES IN Y ...
Page 158
... similar results and also described a ZrF4 - ThF4 binary containing 50-75 - mole % ZrF4 . The latter system was also discussed by Matecki et al . ( 1978 , 1982a ) . Binary fluorozirconate systems containing CaF2 , SrF2 , or PbF2 were ...
... similar results and also described a ZrF4 - ThF4 binary containing 50-75 - mole % ZrF4 . The latter system was also discussed by Matecki et al . ( 1978 , 1982a ) . Binary fluorozirconate systems containing CaF2 , SrF2 , or PbF2 were ...
Contents
vii | 57 |
RONALD E LOEHMAN 119 Sandia National Laboratories Albuquerque | 119 |
HeavyMetal Fluoride Glasses | 151 |
Copyright | |
3 other sections not shown
Common terms and phrases
absorption coefficient AlF3 analysis Basis for Nuclear bead seal behavior Bendow borosilicate glass bulk glasses bulk modulus CCl4 Ceram chemical composite sphere constant cooling corrosion crystalline crystallization curve dB/km devices dielectric Drexhage effects elastic electrical electron energy fibers fluorohafnate fluorozirconate glasses fused silica glass formation glass transition glass transition temperature glass-clad glass-forming region heavy-metal fluoride glasses increase interface traps ions layers leachability leaching Loehman Lucas materials measured melt metal Mitachi modulus MOSFET Moynihan nitride nitrogen Non-Cryst Nuclear Waste Nuclear Waste Management observed optical optical fibers oxide glasses oxynitride glasses Phys Poulain properties Radioactive Waste radionuclides refractive index Rekhson result sample sandwich seal Scherer seal Eq setting temperature shown in Fig silicon SiO2 SiO2 films Solids solution split ring stiffness ratio stress relaxation structural relaxation studies Subsection substrate surface Table techniques thermal thickness viscoelastic viscosity vitreous vitrification Waste Management waste-glass forms wavelength ZBLA ZBLAN ZrF4