... weld defining the design criteria of DFF = 2 i.e. BDFF - 2 2.1 is not satisfied . Including weld improvement by grinding , the reliability curve will be above the reliability curve for the fictitious welds i.e. BDFF - 2 = 2.1 is ...
... weld defining the design criteria of DFF = 2 i.e. BDFF - 2 2.1 is not satisfied . Including weld improvement by grinding , the reliability curve will be above the reliability curve for the fictitious welds i.e. BDFF - 2 = 2.1 is ...
Page 940
... welding procedure as demonstrated by measurements of defects in completed welds in structures and coupons [ 29 ] . In other words , the defect size is justified based on probability of occurrence . Weld Toe Flaw The different weld toe ...
... welding procedure as demonstrated by measurements of defects in completed welds in structures and coupons [ 29 ] . In other words , the defect size is justified based on probability of occurrence . Weld Toe Flaw The different weld toe ...
Page 949
Measurements of local weld toe angle and radius for many specimens were used to construct frequency distributions for these parameters . For a simulation , the weld toe is divided into equal increments , 6 mm long , and values for local ...
Measurements of local weld toe angle and radius for many specimens were used to construct frequency distributions for these parameters . For a simulation , the weld toe is divided into equal increments , 6 mm long , and values for local ...
Contents
OMAE2000OSU OFT3007 | 878 |
I | 879 |
OMAE2000OSU OFT4061 147 | 894 |
Copyright | |
39 other sections not shown
Other editions - View all
Common terms and phrases
alloys application ASME assessment axial bending buckling calculated coefficient composite Copyright corrosion crack growth CTOD cycles deformation depth displacement distribution DQEM drag coefficient drilling fluid Engineering equation failure fatigue crack Figure finite element fire flexible pipe flow flowline FM analysis fracture mechanics function grade gradient hammer peening increase initial inspection installation insulation interlayer layer length lift coefficient material maximum method mode operation parameters peening pipeline plastic plate predicted pressure probabilistic production propagation properties PWHT reduced velocity reliability resistance riser seabed shear shielding gas shown simulation SINTEF SN curves soil span specimens Statoil steel strain strength stress intensity factor stress range surface Table temperature tensile thermal thickness titanium tubular joints tundra turbidity current values vertical loop vessel weld metal weld toe yield strength yield stress Zeepipe