Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 18, Part 4American Society of Mechanical Engineers, 1999 - Arctic regions |
From inside the book
Results 1-3 of 25
Page 69
CCA ( Compact crack Arrest ) specimens were used in size and W = 69 mm for small size . the test with the introduction of brittle weld metal into the crack tip of starting notch by depositing a weld across the specimen thickness with ...
CCA ( Compact crack Arrest ) specimens were used in size and W = 69 mm for small size . the test with the introduction of brittle weld metal into the crack tip of starting notch by depositing a weld across the specimen thickness with ...
Page 70
... crack running until the crack driving force is smaller than the material's crack resistance . There is still a controversy about effect of crack growth path on fracture process . Some authors argue insisted that the emergence of secondary ...
... crack running until the crack driving force is smaller than the material's crack resistance . There is still a controversy about effect of crack growth path on fracture process . Some authors argue insisted that the emergence of secondary ...
Page 86
... CRACK GROWTH The fracture mechanics approach , used to estimate the rate of crack growth , by its nature , does not consider crack initiation . Therefore a small pre - existing flaw ( i.e. a 0.1 mm deep crack ) is assumed to exist at ...
... CRACK GROWTH The fracture mechanics approach , used to estimate the rate of crack growth , by its nature , does not consider crack initiation . Therefore a small pre - existing flaw ( i.e. a 0.1 mm deep crack ) is assumed to exist at ...
Contents
PIPELINE RELIABILITY AND LIMIT STATES DESIGN | 1 |
DESIGN OF PIPELINES AND RISERS | 5 |
OMAE99PIPE5019 | 21 |
Copyright | |
30 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied Arctic Engineering ASME assessment autoclave axial force bending buckling calculated capacity Conference On Offshore Copyright corrosion corrosion defect crack defined deformation dent depth Det Norske Veritas developed diameter discrete displacement vector effect equation failure modes failure probability Figure finite element finite element analysis fracture friction function fuzzy logic gasket geotechnical engineering GTAW hoop stress hot tap tee InSAR installation internal pressure jumper length Limit State Design load longitudinal MANAVGAT material maximum measured Mechanics and Arctic modal displacement neural networks node Offshore Mechanics operating pressure ovalisation parameters Petrobras pipe material pipe wall pipeline design Pipeline Systems plastic reliability riser risk run pipe saddle safety class seabed simulation SMAW SMYS specimens stinger strain stress Table Technology temperature tensile test scheme uprating valve wall thickness yield strength ας მთ მი მს