... brass and copper ) . The galvanic series is not completely predictive , because the ranking is made for seawater as the electrolyte . The series may vary with differences in temperature , agitation , and electrolyte . In most cases ...
... brass and copper ) . The galvanic series is not completely predictive , because the ranking is made for seawater as the electrolyte . The series may vary with differences in temperature , agitation , and electrolyte . In most cases ...
Page 11
... brass , containing 35 percent zinc , is easier to machine than red brass , but is susceptible to stress corrosion cracking . Chemical resistance of the high- zinc brasses is only fair , and they are not suitable for use in photographic ...
... brass , containing 35 percent zinc , is easier to machine than red brass , but is susceptible to stress corrosion cracking . Chemical resistance of the high- zinc brasses is only fair , and they are not suitable for use in photographic ...
Page 13
... Brass Yellow Brass Admiralty Brass NICKEL Nickel ( Pure ) Duranickel Cu 88.35 , Ni 10 , Fe 1.25 , Mn 0.4 0.323 27 127 9.3 600 315 18 44 15 Cu 99.9 + 0.323 222 Cu 85 , Zn 15 0.316 22222 9.2 400 205 17 32 92 10.4 450 230 17 40 20 10 12 ON ...
... Brass Yellow Brass Admiralty Brass NICKEL Nickel ( Pure ) Duranickel Cu 88.35 , Ni 10 , Fe 1.25 , Mn 0.4 0.323 27 127 9.3 600 315 18 44 15 Cu 99.9 + 0.323 222 Cu 85 , Zn 15 0.316 22222 9.2 400 205 17 32 92 10.4 450 230 17 40 20 10 12 ON ...
Common terms and phrases
Acetate acids added AISI Type alcohol alkalies alloy anodic applications aromatic attack base bleaches brass carbon cast cause Cellulose Cellulose Acetate chemical resistance chloride Coating common Company compounds concentration construction materials containing continuous copper corrosion developer dilute dimensional stability DuPont effect elastomers environment Epoxy excellent fabrication Fe balance Fiber filter Flexible Glass grades graphic hardness heat Hypalon impact important increases Industries inhibitors iron lines machine material mechanical metal molding Nemours occurs organic oxidizing percent Phenolic photographic activity photographic processing equipment photographic processing solutions physical piping pitting plastics Polyester Polyethylene polymer Polypropylene Polyvinyl Chloride prior problems proper properties protective range ratio recommended Reinforced resins rubber satisfactory selection Silicone soften solvents stainless steel strength strong suitable sulfur surface Table tanks techniques Teflon temperature thermoplastic tions usually welding wide