Page 6
... Stress - Corrosion Cracking . Stress - corrosion crack- ing refers to cracking caused by a combination of tensile stress and a specific corrodent . It is usually highly localized and insidious . Common methods of avoiding stress ...
... Stress - Corrosion Cracking . Stress - corrosion crack- ing refers to cracking caused by a combination of tensile stress and a specific corrodent . It is usually highly localized and insidious . Common methods of avoiding stress ...
Page 20
... stress - cracking , and decom- position of the part . Some photographic activity has been noted in developer ... stress - corrosion cracking . Testing is strongly rec- ommended before use . Environmental - stress crack- ing is 20.
... stress - cracking , and decom- position of the part . Some photographic activity has been noted in developer ... stress - corrosion cracking . Testing is strongly rec- ommended before use . Environmental - stress crack- ing is 20.
Page 21
Eastman Kodak Company. ommended before use . Environmental - stress crack- ing is due to the premature failure of polyethylene in the presence of active chemicals under conditions of relatively high strain . Stress - cracking resistance ...
Eastman Kodak Company. ommended before use . Environmental - stress crack- ing is due to the premature failure of polyethylene in the presence of active chemicals under conditions of relatively high strain . Stress - cracking resistance ...
Common terms and phrases
Acetate acids added AISI Type alcohol alkalies alloy anodic applications aromatic attack base bleaches brass carbon cast cause Cellulose Cellulose Acetate chemical resistance chloride Coating common Company compounds concentration construction materials containing continuous copper corrosion developer dilute dimensional stability DuPont effect elastomers environment Epoxy excellent fabrication Fe balance Fiber filter Flexible Glass grades graphic hardness heat Hypalon impact important increases Industries inhibitors iron lines machine material mechanical metal molding Nemours occurs organic oxidizing percent Phenolic photographic activity photographic processing equipment photographic processing solutions physical piping pitting plastics Polyester Polyethylene polymer Polypropylene Polyvinyl Chloride prior problems proper properties protective range ratio recommended Reinforced resins rubber satisfactory selection Silicone soften solvents stainless steel strength strong suitable sulfur surface Table tanks techniques Teflon temperature thermoplastic tions usually welding wide