Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3American Society of Mechanical Engineers, 1993 - Arctic regions |
From inside the book
Results 1-3 of 64
Page 60
... Charpy and tensile testing . The heat treatment was carried out at 750 ° C for 40 , 55 and 65 minutes to obtain nominal sigma levels of 2.5 , 5 and 13 percent , respectively . To optimise the use of the test pieces special procedures ...
... Charpy and tensile testing . The heat treatment was carried out at 750 ° C for 40 , 55 and 65 minutes to obtain nominal sigma levels of 2.5 , 5 and 13 percent , respectively . To optimise the use of the test pieces special procedures ...
Page 67
... Charpy impact energy / lateral expansion is depicted in Fig.11 . To minimise variability , only the Charpy and CTOD values obtained from the same end of a given pipe section were correlated . Although some scatter is obvious from the ...
... Charpy impact energy / lateral expansion is depicted in Fig.11 . To minimise variability , only the Charpy and CTOD values obtained from the same end of a given pipe section were correlated . Although some scatter is obvious from the ...
Page 221
... Charpy test temperature , " C FIGURE 3 ( a ) · Charpy Vee uansition curves for coarse HAZ region of welded steel C as a function of heat input FIGURE 3 ( b ) . 300 o 1.5 KJ / am O 3.0 XJ / mm △ 6.0 XJ / mn 6.0 -100 -40 -60 -60 -20 ...
... Charpy test temperature , " C FIGURE 3 ( a ) · Charpy Vee uansition curves for coarse HAZ region of welded steel C as a function of heat input FIGURE 3 ( b ) . 300 o 1.5 KJ / am O 3.0 XJ / mm △ 6.0 XJ / mn 6.0 -100 -40 -60 -60 -20 ...
Contents
HIGH STRENGTH STEELS FOR OFFSHORE | 189 |
WELDING CONTROL | 265 |
APPLICATIONS OF GRP OFFSHORE | 279 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied argon artificial neural network ASTM austenite austenite grain bainite base metal behaviour bending CGHAZ Charpy composite pipe cooling corrosion crack propagation CTOD curve cycles developed diameter effect elastomer electrodes Engineering ASME 1993 epoxy equation evaluation fabrication factor ferrite finite element firewater flange fracture fracture mechanics GRE pipe heat input high strength steels HSLA HSLA steels hydrogen increase installation intumescent kJ/mm load martensite Materials Engineering ASME maximum method microstructure MIRT nitrogen nitrogen steel node notch offshore structures OMAE parameters performance predicted preheat pressure procedures PWHT range reduced S-N curves seal seawater sheave shielding gas shown in Figure simulated SINTEF specimens spool stainless steel strain surface Table Technology temperature tensile test results thickness toughness tubular joints underwater Underwater Welding values weld metal weldability welded joints weldments wet welding wide plate wire yield strength