... carbon equivalents have been included . The CIIW [ 2 ] and the Pcm [ 4 ] are the most frequently used . The two other carbon equivalents are the CEN and the CEPLS . The CEN carbon equivalent was proposed by Yurioka et . al . [ 5 ] and ...
... carbon equivalents have been included . The CIIW [ 2 ] and the Pcm [ 4 ] are the most frequently used . The two other carbon equivalents are the CEN and the CEPLS . The CEN carbon equivalent was proposed by Yurioka et . al . [ 5 ] and ...
Page 78
... carbon steel weld metal . The effects of alloying on the strength of low- carbon weld metals was obtained from two different welding procedures . First , autogenous welds were pro- duced in a series of low - carbon steel model materials ...
... carbon steel weld metal . The effects of alloying on the strength of low- carbon weld metals was obtained from two different welding procedures . First , autogenous welds were pro- duced in a series of low - carbon steel model materials ...
Page 410
... CARBON DIOXIDE BY VARIOUS TYPES OF ELASTOMERS 500 250 70C 100C 155C 195C EFFECT OF TEMPERATURE ON GAS UPTAKE One must not be misled into applying such information as that above to other gases , or to carbon dioxide at other temperatures ...
... CARBON DIOXIDE BY VARIOUS TYPES OF ELASTOMERS 500 250 70C 100C 155C 195C EFFECT OF TEMPERATURE ON GAS UPTAKE One must not be misled into applying such information as that above to other gases , or to carbon dioxide at other temperatures ...
Contents
HIGH STRENGTH STEELS FOR OFFSHORE | 189 |
WELDING CONTROL | 265 |
APPLICATIONS OF GRP OFFSHORE | 279 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied argon artificial neural network ASTM austenite austenite grain bainite base metal behaviour bending CGHAZ Charpy composite pipe cooling corrosion crack propagation CTOD curve cycles developed diameter effect elastomer electrodes Engineering ASME 1993 epoxy equation evaluation fabrication factor ferrite finite element firewater flange fracture fracture mechanics GRE pipe heat input high strength steels HSLA HSLA steels hydrogen increase installation intumescent kJ/mm load martensite Materials Engineering ASME maximum method microstructure MIRT nitrogen nitrogen steel node notch offshore structures OMAE parameters performance predicted preheat pressure procedures PWHT range reduced S-N curves seal seawater sheave shielding gas shown in Figure simulated SINTEF specimens spool stainless steel strain surface Table Technology temperature tensile test results thickness toughness tubular joints underwater Underwater Welding values weld metal weldability welded joints weldments wet welding wide plate wire yield strength