... fabrication , in terms of the requirement for less stringent welding precautions during fabrication . Five steels of 690MPa nominal yield strength with good toughness and which were available in 50mm thick section were selected for ...
... fabrication , in terms of the requirement for less stringent welding precautions during fabrication . Five steels of 690MPa nominal yield strength with good toughness and which were available in 50mm thick section were selected for ...
Page 193
... fabrication by the avoidance of preheat if suitable welding processes and consumables , such as FCAW , were specified . In practical fabrication of large structures , the SAW process is currently widely used and many difficulties could ...
... fabrication by the avoidance of preheat if suitable welding processes and consumables , such as FCAW , were specified . In practical fabrication of large structures , the SAW process is currently widely used and many difficulties could ...
Page 255
... fabricated part of the node . solution ( fig 9 ) demonstrates just how a casting can be which then only relatively simple cost effective used in an optimised node form requires relatively simple fabrication to complete . Spreader Bar ...
... fabricated part of the node . solution ( fig 9 ) demonstrates just how a casting can be which then only relatively simple cost effective used in an optimised node form requires relatively simple fabrication to complete . Spreader Bar ...
Contents
HIGH STRENGTH STEELS FOR OFFSHORE | 189 |
WELDING CONTROL | 265 |
APPLICATIONS OF GRP OFFSHORE | 279 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied argon artificial neural network ASTM austenite austenite grain bainite base metal behaviour bending CGHAZ Charpy composite pipe cooling corrosion crack propagation CTOD curve cycles developed diameter effect elastomer electrodes Engineering ASME 1993 epoxy equation evaluation fabrication factor ferrite finite element firewater flange fracture fracture mechanics GRE pipe heat input high strength steels HSLA HSLA steels hydrogen increase installation intumescent kJ/mm load martensite Materials Engineering ASME maximum method microstructure MIRT nitrogen nitrogen steel node notch offshore structures OMAE parameters performance predicted preheat pressure procedures PWHT range reduced S-N curves seal seawater sheave shielding gas shown in Figure simulated SINTEF specimens spool stainless steel strain surface Table Technology temperature tensile test results thickness toughness tubular joints underwater Underwater Welding values weld metal weldability welded joints weldments wet welding wide plate wire yield strength