... Steel Corporation Kimitsu City , Japan ABSTRACT Titanium - oxide bearing steel ( Ti - O steel ) , which has improved toughness in the heat - affected zone ( HAZ ) by utilizing intragranular ferrite ( IGF ) , has been devel- oped , and ...
... Steel Corporation Kimitsu City , Japan ABSTRACT Titanium - oxide bearing steel ( Ti - O steel ) , which has improved toughness in the heat - affected zone ( HAZ ) by utilizing intragranular ferrite ( IGF ) , has been devel- oped , and ...
Page 217
... steel B and the normalised and tempered steel with the highest hardenability , steel C , would not be suitable for welding at 3kJ / mm and above . However , the quenched and tempered steels , D , E and A , could all be welded at high ...
... steel B and the normalised and tempered steel with the highest hardenability , steel C , would not be suitable for welding at 3kJ / mm and above . However , the quenched and tempered steels , D , E and A , could all be welded at high ...
Page 236
... steel A is still expected to have larger austenite grains than steel B. At 1350 ° C , TIN begins to dissolve and because of the higher nitrogen content in steel B , the TIN precipitates in steel B are more stable and resistant to ...
... steel A is still expected to have larger austenite grains than steel B. At 1350 ° C , TIN begins to dissolve and because of the higher nitrogen content in steel B , the TIN precipitates in steel B are more stable and resistant to ...
Contents
HIGH STRENGTH STEELS FOR OFFSHORE | 189 |
WELDING CONTROL | 265 |
APPLICATIONS OF GRP OFFSHORE | 279 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied argon artificial neural network ASTM austenite austenite grain bainite base metal behaviour bending CGHAZ Charpy composite pipe cooling corrosion crack propagation CTOD curve cycles developed diameter effect elastomer electrodes Engineering ASME 1993 epoxy equation evaluation fabrication factor ferrite finite element firewater flange fracture fracture mechanics GRE pipe heat input high strength steels HSLA HSLA steels hydrogen increase installation intumescent kJ/mm load martensite Materials Engineering ASME maximum method microstructure MIRT nitrogen nitrogen steel node notch offshore structures OMAE parameters performance predicted preheat pressure procedures PWHT range reduced S-N curves seal seawater sheave shielding gas shown in Figure simulated SINTEF specimens spool stainless steel strain surface Table Technology temperature tensile test results thickness toughness tubular joints underwater Underwater Welding values weld metal weldability welded joints weldments wet welding wide plate wire yield strength