Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3American Society of Mechanical Engineers, 1993 - Arctic regions |
From inside the book
Results 1-3 of 83
Page 69
... wires , and seven metal cored wires were tested . G - BOP testing was performed at ambient but also at higher temperatures so that the preheating temperature could be evaluated . Gas shielding was used , wire diameter being 1.2 and 1.6 ...
... wires , and seven metal cored wires were tested . G - BOP testing was performed at ambient but also at higher temperatures so that the preheating temperature could be evaluated . Gas shielding was used , wire diameter being 1.2 and 1.6 ...
Page 70
... wire and flux . Baking the flux or the finished wire at 700 to 800 ° C gave weld metal hydrogen contents well below 5 ml / 100 g of as deposited weld metal . In a Danish MSc thesis in 1983 a very large number of commercial cored wires ...
... wire and flux . Baking the flux or the finished wire at 700 to 800 ° C gave weld metal hydrogen contents well below 5 ml / 100 g of as deposited weld metal . In a Danish MSc thesis in 1983 a very large number of commercial cored wires ...
Page 88
... wire compared with cold wire GTAW process in case of CRA pipeli- ne welding . For reference purposes a conclusive diagram is reported ( Fig . 12 ) , showing the laying productivity ( and consequently the laying costs ) for a CRA ...
... wire compared with cold wire GTAW process in case of CRA pipeli- ne welding . For reference purposes a conclusive diagram is reported ( Fig . 12 ) , showing the laying productivity ( and consequently the laying costs ) for a CRA ...
Contents
HIGH STRENGTH STEELS FOR OFFSHORE | 189 |
WELDING CONTROL | 265 |
APPLICATIONS OF GRP OFFSHORE | 279 |
Copyright | |
10 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied argon artificial neural network ASTM austenite austenite grain bainite base metal behaviour bending CGHAZ Charpy composite pipe cooling corrosion crack propagation CTOD curve cycles developed diameter effect elastomer electrodes Engineering ASME 1993 epoxy equation evaluation fabrication factor ferrite finite element firewater flange fracture fracture mechanics GRE pipe heat input high strength steels HSLA HSLA steels hydrogen increase installation intumescent kJ/mm load martensite Materials Engineering ASME maximum method microstructure MIRT nitrogen nitrogen steel node notch offshore structures OMAE parameters performance predicted preheat pressure procedures PWHT range reduced S-N curves seal seawater sheave shielding gas shown in Figure simulated SINTEF specimens spool stainless steel strain surface Table Technology temperature tensile test results thickness toughness tubular joints underwater Underwater Welding values weld metal weldability welded joints weldments wet welding wide plate wire yield strength