Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 5American Society of Mechanical Engineers, 1993 - Arctic regions |
From inside the book
Results 1-3 of 85
Page 219
... surface . The fracture surface of the specimens tested in the artificial sea water was carefully observed to find the secondary cracking . Figure 11 shows the SEM ( Scanning Electron Microscope ) images of the fracture surfaces of the ...
... surface . The fracture surface of the specimens tested in the artificial sea water was carefully observed to find the secondary cracking . Figure 11 shows the SEM ( Scanning Electron Microscope ) images of the fracture surfaces of the ...
Page 226
... surfaces . This three - year program for the Pipeline Research Committee ( PRC ) of the A.G.A. focused on these three factors ( disbonding resistance , the ability to pass CP current , and surface preparation ) and SCC susceptibility ...
... surfaces . This three - year program for the Pipeline Research Committee ( PRC ) of the A.G.A. focused on these three factors ( disbonding resistance , the ability to pass CP current , and surface preparation ) and SCC susceptibility ...
Page 227
... surface moves it further away from the cracking range , regardless of the geometry of the disbonded region . This effect may be important immediately following coating disbondment . However , once the pipe surface has been exposed to ...
... surface moves it further away from the cracking range , regardless of the geometry of the disbonded region . This effect may be important immediately following coating disbondment . However , once the pipe surface has been exposed to ...
Contents
OFFSHORE | 1 |
Mechanical Properties of | 22 |
Ice Engineering | 80 |
Copyright | |
14 other sections not shown
Other editions - View all
Common terms and phrases
Almen strip anticorrosion coating applied assessment axial force backfill behaviour bending Bruschi buckle buckle lengths burst pressure calculated cathodic protection circumferential coefficients compression concrete coating configuration crack propagation criteria curvature deformation depth developed diameter directional drill disbonded displacement ditch effect Engineering equations factor failure fatigue field joints flow fracture free spans gas pipeline grit blasting hoop stress hydrodynamic increase installation interaction layer length load longitudinal material maximum measured mechanical metal loss monitoring NACE niobium Offshore operating OTDR overcoating parameters pile pipeline pits plastic Polypropylene predicted resistance response sand scour seabed self-lowering sensor settlement shear shear strength shown in Figure simulated Snamprogetti soil solution specimens Statoil steel stiffness strain strain gauges strength stress stress concentration structural surface temperature thickness TMCP uneven seabed values velocity wave weld Zeepipe zone