... annealing twins in an fcc gold - silver alloy . Annealing twins are usually broader and with straighter sides than mechanical twins . The energy of annealing twin boundaries is about 5 per cent of the average grain - boundary energy ...
... annealing twins in an fcc gold - silver alloy . Annealing twins are usually broader and with straighter sides than mechanical twins . The energy of annealing twin boundaries is about 5 per cent of the average grain - boundary energy ...
Page 153
... annealing . Annealing is very impor- tant commercially because it restores the ductility to a metal that has been severely strain - hardened . Therefore , by interposing annealing operations after severe deformation it is possible to ...
... annealing . Annealing is very impor- tant commercially because it restores the ductility to a metal that has been severely strain - hardened . Therefore , by interposing annealing operations after severe deformation it is possible to ...
Page 156
... Anneal- ing - texture formation depends on a number of processing variables , the amount and type of deformation preceding annealing , the composition of the alloy , the grain size , the annealing temperature and time , and the ...
... Anneal- ing - texture formation depends on a number of processing variables , the amount and type of deformation preceding annealing , the composition of the alloy , the grain size , the annealing temperature and time , and the ...
Contents
Introduction | 5 |
The Torsion Test | 10 |
Stress and Strain Relationships for Elastic Behavior | 17 |
Copyright | |
22 other sections not shown
Other editions - View all
Common terms and phrases
alloys aluminum annealing ASTM axis behavior brittle fracture Burgers vector cent compressive considered constant crack decrease determined diameter dislocation line ductile edge dislocation effect elastic elongation equation factor fatigue limit fatigue properties flow curve fracture stress given grain boundaries hardness increase indentation internal friction lattice load martensite material maximum measure Metals Park modulus notch number of cycles occurs orientation particles pile-up plastic deformation principal stresses Proc produced quenched ratio recrystallization reduction of area region residual stresses resolved shear stress screw dislocations shear stress shown shows single crystals slip direction slip lines slip plane slip system Society for Metals solid solution solute atoms specimen stacking fault steel strain energy strain hardening strain rate stress concentration stress-strain curve structure surface tensile strength tensile stress tension theory tion torsion Trans twins vacancies yield point yield strength yield stress