MECHANICAL METALLURGY |
From inside the book
Results 1-3 of 46
Page 269
... ( longitudinal ) direction of working may be greater or less than the yield strength in the longitudinal direction , depending upon the type of preferred orientation which exists . This type of ani- sotropy is most frequently found in ...
... ( longitudinal ) direction of working may be greater or less than the yield strength in the longitudinal direction , depending upon the type of preferred orientation which exists . This type of ani- sotropy is most frequently found in ...
Page 405
... longitudinal residual stress at the surface is given by ( 15-11 ) Round Bar στ E't8 2L2 ( 15-12 ) The same procedure can be used to estimate the surface longitudinal stress in a round bar1 ( Fig . 15-6b ) . With the notation given in ...
... longitudinal residual stress at the surface is given by ( 15-11 ) Round Bar στ E't8 2L2 ( 15-12 ) The same procedure can be used to estimate the surface longitudinal stress in a round bar1 ( Fig . 15-6b ) . With the notation given in ...
Page 547
... longitudinal residual For larger reductions of commercial significance the residual- stress distribution is completely reversed from the first type of stress pattern . In this case the longitudinal stresses are tensile at the surface ...
... longitudinal residual For larger reductions of commercial significance the residual- stress distribution is completely reversed from the first type of stress pattern . In this case the longitudinal stresses are tensile at the surface ...
Contents
Introduction | 5 |
The Torsion Test | 10 |
Stress and Strain Relationships for Elastic Behavior | 17 |
Copyright | |
22 other sections not shown
Other editions - View all
Common terms and phrases
alloys aluminum annealing ASTM axis behavior brittle fracture Burgers vector cent compressive considered constant crack decrease determined diameter dislocation line ductile edge dislocation effect elastic elongation equation factor fatigue limit fatigue properties flow curve fracture stress given grain boundaries hardness increase indentation internal friction lattice load martensite material maximum measure Metals Park modulus notch number of cycles occurs orientation particles pile-up plastic deformation principal stresses Proc produced quenched ratio recrystallization reduction of area region residual stresses resolved shear stress screw dislocations shear stress shown shows single crystals slip direction slip lines slip plane slip system Society for Metals solid solution solute atoms specimen stacking fault steel strain energy strain hardening strain rate stress concentration stress-strain curve structure surface tensile strength tensile stress tension theory tion torsion Trans twins vacancies yield point yield strength yield stress