Microstructure of Cement-Based Systems: Volume 370: Bonding and Interfaces in Cementitious MaterialsThis book continues the MRS series on characteristics and properties of cementitious materials. In Part I, recent advances in microstructure and related characterization of cementitious systems are the focus. Topics include: microstructures of "normal" cement systems; microstructure of 'unusual' cement systems; image analysis, modelling and fractal analysis applications; and assessment of pore structures. Part II features presentations on interfacial microstructures, as well as information on elastic and fracture properties, transport properties, and the effects of interfaces on fiber-reinforced systems. |
From inside the book
Results 1-3 of 46
Page 211
... Compressive strength The 28 day compressive strengths of mixes of different concentrations are presented in Figure 1. It can be seen that increasing the concentration of the simulated LLW from 5.5 % to 33 % of the values given in Table ...
... Compressive strength The 28 day compressive strengths of mixes of different concentrations are presented in Figure 1. It can be seen that increasing the concentration of the simulated LLW from 5.5 % to 33 % of the values given in Table ...
Page 420
... compressive strength of concrete . EXPERIMENTAL STUDIES MODIFYING INTERFACIAL BOND STRENGTH There are two aspects of interfacial strength : 1 ) the strength of the paste in the interfacial transition zone itself and 2 ) the bond strength ...
... compressive strength of concrete . EXPERIMENTAL STUDIES MODIFYING INTERFACIAL BOND STRENGTH There are two aspects of interfacial strength : 1 ) the strength of the paste in the interfacial transition zone itself and 2 ) the bond strength ...
Page 424
... compressive strength of concrete . EXPERIMENTAL STUDIES MODIFYING PASTE CONSTITUENT The use of silica fume as a cement replacement has been shown to result in significant in- creases in the strength of concrete7 , 14 , 16 , 17 , 19 , 20 ...
... compressive strength of concrete . EXPERIMENTAL STUDIES MODIFYING PASTE CONSTITUENT The use of silica fume as a cement replacement has been shown to result in significant in- creases in the strength of concrete7 , 14 , 16 , 17 , 19 , 20 ...
Contents
APPLICATION OF AUTOMATED IMAGE ANALYSIS TO | 3 |
A REEVALUATION OF HARDENED CEMENT PASTE | 13 |
AN APPROACH TO QUANTITATIVE IMAGE ANALYSIS | 23 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
1995 Materials Research air voids andesite bond strength bulk cement paste C-S-H gel calcium calcium hydroxide carbonate cement paste cementitious chemical clinker composite compressive strength concentration Concr crack crystals cured curve debonding density diameter dielectric diffusion dynamic modulus effect elastic elastic moduli embedded length energy ettringite experimental fiber reinforced fibres fly ash fracture surface Garboczi grains groundmass hardened hydration products image analysis increase interfacial transition zone interfacial zone load Materials Research Society matrix measured microcracks microscope microstructure mixes modulus mortar observed parameters phase pore size distribution porosity porous portland cement portlandite Proc pullout rock samples sand scanning electron microscope shear shown in Figure shows silica fume solution specimens stress structure sucrose superplasticizer Symp Table tensile thaumasite thickness values volume fraction w/c ratio water-cement ratio wood fiber yarn zeolite