Treatise on Materials Science and TechnologyHerbert Herman |
From inside the book
Results 1-3 of 53
Page 329
Herbert Herman. From the A values listed in Table VIII , GdIG with an A of 1.0007 has the lowest anistropy , YGaG with an A of 1.10 has the highest anisotropy . Most of the listed A values in Table VIII lie within ± 5 % of isotropy . TABLE ...
Herbert Herman. From the A values listed in Table VIII , GdIG with an A of 1.0007 has the lowest anistropy , YGaG with an A of 1.10 has the highest anisotropy . Most of the listed A values in Table VIII lie within ± 5 % of isotropy . TABLE ...
Page 355
... Table XVIII . As discussed in Section III , E and shown in Fig . 14 , there are six nonequivalent c - sites in the ... Table XIV . The g , direction can be either the a axis or the b axis , and the selection is arbitrary . The g - factor ...
... Table XVIII . As discussed in Section III , E and shown in Fig . 14 , there are six nonequivalent c - sites in the ... Table XIV . The g , direction can be either the a axis or the b axis , and the selection is arbitrary . The g - factor ...
Page 360
... ( Table XIX ) . From the optical spectra , the energy levels of the ground state multiplets of trivalent rare - earth ions in garnets can be determined and are listed in Table XXII ( Oliver et al . , 1969a ) . 1 The refractive index of ...
... ( Table XIX ) . From the optical spectra , the energy levels of the ground state multiplets of trivalent rare - earth ions in garnets can be determined and are listed in Table XXII ( Oliver et al . , 1969a ) . 1 The refractive index of ...
Contents
Epitaxial Interfaces | 3 |
Thin Films | 15 |
Semiinfinite Overgrowths | 37 |
Copyright | |
11 other sections not shown
Common terms and phrases
a-site alloy Amer anisotropy Appl approximation atoms average axis B₁ Bragg Bragg reflections c-sites calculated cations coefficients coherent compounds concentration configuration constant Cooper pairs curve Debye-Waller factor defect density dependence discussed displacement elastic electron energy epitaxial equation experimental factor ferrimagnetic field film flux lines function garnet garnet structure GdIG Geller IAEA impurity Inelastic Scattering interaction interface iron garnets k₁ lattice constant lattice parameter Lett magnetic magnetocrystalline anisotropy measured Merwe method misfit misfit dislocations mode neutron scattering normal obtained overgrowth phase phonon Phys plane potential Proc properties rare earth rare earth ions reciprocal lattice resolution sample scattering cross section shown in Fig single crystal small angle solid strain stress sublattice substrate superconducting surface symmetry Table temperature tetrahedral thermal thickness transition metal values vector X-ray YGaG