## Treatise on Materials Science and Technology, Volume 2 |

### From inside the book

Results 1-3 of 29

Page 122

Many monatomic crystals have

the table ) . For such elements ( e . g . , Au , Al , Cu ) the diffusional line

broadening is not observable with neutron techniques . The diffusional

broadening of the ...

Many monatomic crystals have

**diffusion**coefficients similar to nickel ( shown inthe table ) . For such elements ( e . g . , Au , Al , Cu ) the diffusional line

broadening is not observable with neutron techniques . The diffusional

broadening of the ...

Page 197

64 ) ] we remember that for K•a < 1 the linewidth of the incoherent quasielastic

scattering is given by the

neutron scattering as the actual macroscopic bulk

...

64 ) ] we remember that for K•a < 1 the linewidth of the incoherent quasielastic

scattering is given by the

**diffusion**constant : AW1 = 2Dk2 . D is determined byneutron scattering as the actual macroscopic bulk

**diffusion**coefficient for a crystal...

Page 327

2 kcal (

LaFe204 has a Do of 1 . 6 and of 85 kcal , and the La

10 - 2 and Q of 65 . 0 kcal . Between 1240° and 1420°C , the Fe

2 kcal (

**Diffusion**Data , 1969 ) . Between 1240° and 1420°C , the Fe**diffusion**inLaFe204 has a Do of 1 . 6 and of 85 kcal , and the La

**diffusion**has a Do of 3 . 7 x10 - 2 and Q of 65 . 0 kcal . Between 1240° and 1420°C , the Fe

**diffusion**has a ...### What people are saying - Write a review

We haven't found any reviews in the usual places.

### Contents

Epitaxial Interfaces | 3 |

Thin Films | 15 |

Semiinfinite Overgrowths | 52 |

Copyright | |

10 other sections not shown

### Other editions - View all

### Common terms and phrases

angle anisotropy approximation assumed atoms average axis c-site calculated cations coherent compounds concentration condition considerations constants contribution corresponding crystal curve decreases defect density dependence determined diffusion direction discussed dislocations displacement effect elastic elastic scattering electron energy equation et al experimental experiments factor field flux flux lines follows force function garnets given gives important impurity increases interaction interface ions lattice limit magnetic materials measured Merwe metal method misfit mode neutron normal observed obtained optical parameter phase phonon Phys plane position potential present processes properties range reference region resolution respectively sample scattering cross section shown shows single solid solution space strain stress structure substrate superconducting surface Table temperature tetrahedral theory thermal thickness transition unit values vector wave X-ray