... methods , however , measure the gradients near the surface , and great care is required to eliminate surface pinning . Direct observation of flux distributions and their changes are possible by use of the Faraday effect . The method was ...
... methods , however , measure the gradients near the surface , and great care is required to eliminate surface pinning . Direct observation of flux distributions and their changes are possible by use of the Faraday effect . The method was ...
Page 319
... METHOD The flux growth method uses liquids as solvents ; mostly molten inorganic compounds at elevated temperatures . Careful cooling of the melt produces crystallization ( Laudise , 1963 ) . The advantages of the flux growth method ...
... METHOD The flux growth method uses liquids as solvents ; mostly molten inorganic compounds at elevated temperatures . Careful cooling of the melt produces crystallization ( Laudise , 1963 ) . The advantages of the flux growth method ...
Page 321
... METHOD The Czochralski method of pulling a crystal from the melt balances the pulling rate and thermal conditions so that growth results without with- drawing the seed . The crystal should melt congruently without decomposition . The ...
... METHOD The Czochralski method of pulling a crystal from the melt balances the pulling rate and thermal conditions so that growth results without with- drawing the seed . The crystal should melt congruently without decomposition . The ...
Contents
Epitaxial Interfaces | 3 |
Thin Films | 15 |
Semiinfinite Overgrowths | 37 |
Copyright | |
11 other sections not shown
Common terms and phrases
angle anisotropy Appl approximation assumed atoms average axis c-sites calculated cations coherent concentration condition considerations constant contribution corresponding crystal curve defect density dependence determined diffusion direction discussed dislocations displacement effect elastic elastic scattering electron energy equation et al exist experimental experiments factor field flux lines follows force function garnet given gives important increasing interaction interface ions lattice length Lett limit magnetic materials measured Merwe metal method misfit mode neutron normal obtained parameter phase phonon Phys plane position potential present properties range rare earth reference region relation resolution respectively sample scattering cross section shown shows single solid solution space strain stress structure substrate superconducting surface Table temperature tetrahedral theory thermal thickness transition unit values vector X-ray