... solvent - solute system , the large number of suitable inorganic solvents , and its special ability to grow incon- gruently melting crystals . Disadvantages lie in the introduction of impurities from the solvents , and the possible ...
... solvent - solute system , the large number of suitable inorganic solvents , and its special ability to grow incon- gruently melting crystals . Disadvantages lie in the introduction of impurities from the solvents , and the possible ...
Page 320
... solvent . The molten solvent is less dense than YIG so that YIG crystals sink in it . e . Flux PbO - PbF2 - B2O3 : Large optical quality crystals ( 60 g for each crystal ) of YAG and ReAG were grown with PbO - PbF2 - B2O3 as the flux ...
... solvent . The molten solvent is less dense than YIG so that YIG crystals sink in it . e . Flux PbO - PbF2 - B2O3 : Large optical quality crystals ( 60 g for each crystal ) of YAG and ReAG were grown with PbO - PbF2 - B2O3 as the flux ...
Page 326
... solvent is 1.8 ; 1.8 for Er ; 1.0 for Y ; 0.9 for Tb ; 0.2 for Sm ; 0.05 for Nd ; and 0.02 for Pr . The data are arranged by decreasing order of rare earth radius ( Monchamp et al . , 1967 ) . The distribution coefficient of Nd in YAG ...
... solvent is 1.8 ; 1.8 for Er ; 1.0 for Y ; 0.9 for Tb ; 0.2 for Sm ; 0.05 for Nd ; and 0.02 for Pr . The data are arranged by decreasing order of rare earth radius ( Monchamp et al . , 1967 ) . The distribution coefficient of Nd in YAG ...
Contents
Epitaxial Interfaces | 3 |
Thin Films | 15 |
Semiinfinite Overgrowths | 37 |
Copyright | |
11 other sections not shown
Common terms and phrases
angle anisotropy Appl approximation assumed atoms average axis c-sites calculated cations coherent concentration condition considerations constant contribution corresponding crystal curve defect density dependence determined diffusion direction discussed dislocations displacement effect elastic elastic scattering electron energy equation et al exist experimental experiments factor field flux lines follows force function garnet given gives important increasing interaction interface ions lattice length Lett limit magnetic materials measured Merwe metal method misfit mode neutron normal obtained parameter phase phonon Phys plane position potential present properties range rare earth reference region relation resolution respectively sample scattering cross section shown shows single solid solution space strain stress structure substrate superconducting surface Table temperature tetrahedral theory thermal thickness transition unit values vector X-ray