... heat source which , in most welds , can be regarded as the weld metal . Heat transfer in the welded joint produces a changing temperature distribution which induces thermal stresses . An important point in the mechanical behavior is ...
... heat source which , in most welds , can be regarded as the weld metal . Heat transfer in the welded joint produces a changing temperature distribution which induces thermal stresses . An important point in the mechanical behavior is ...
Page 46
... heat input welds . In other words , failure to modify one of these requirements will need an impressive amount of ( re ) test to obtain a sufficient number of metallurgical valid CGHAZ CTOD test results . That is , it is techni- cally ...
... heat input welds . In other words , failure to modify one of these requirements will need an impressive amount of ( re ) test to obtain a sufficient number of metallurgical valid CGHAZ CTOD test results . That is , it is techni- cally ...
Page 121
... heat inputs by adop- ting 1/2 V shaped grooves . Detailed SAW conditions are given in Table VI . Some of the welded joints were post weld heat treated ( PWHT ) at 600 ° C for two hours . The HAZ toughness of the two TMCP steels was ...
... heat inputs by adop- ting 1/2 V shaped grooves . Detailed SAW conditions are given in Table VI . Some of the welded joints were post weld heat treated ( PWHT ) at 600 ° C for two hours . The HAZ toughness of the two TMCP steels was ...
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
WELD METAL AND HAZ PROPERTIES | 37 |
The Effect of Intercritical Thermal Cycles on HAZ Microstructure and Toughness in CMnAlNb | 49 |
Copyright | |
14 other sections not shown
Other editions - View all
Common terms and phrases
alloys analysis austenite axial base metal bead behaviour brittle CGHAZ Charpy chemical composition cooling corrosion crack front crack tip critical CTOD CTOD fracture toughness CTOD test CTOD value deformation distribution effect experimental fatigue crack ferrite Figure Fracture Mechanics fusion boundary gauges grain coarsened HAZ groove HAZ region HAZ toughness heat affected zone heat input hydrogen cracking hyperbaric ICCGHAZ inherent strain intercritical kJ/mm load martensite measured mechanical properties method microstructure multi-pass welds narrow gap notched panel obtained OMAE peak temperature pearlite pipe plastic plate thickness Pop-in pressure PWHT reheated samples shielding gas simulation single-U Statoil steel plates steel TM1 strain gauges submerged arc welding surface notched specimen Table tempered tensile thermal cycle through-thickness notched titanium TMCP steel underwater welding weld metal weld passes welded joint welding conditions Welding Institute welding parameters welding procedure welding process welding residual stress weldments width yield strength