Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 10American Society of Mechanical Engineers, 1991 - Arctic regions |
From inside the book
Results 1-3 of 62
Page 223
... lower the sulfur and oxygen contents in order to ensure resistance to lamellar tearing . In addition to this , it is necessary to lower the hydrogen content and reduce segregation in order to ensure the internal quality of steel . To ...
... lower the sulfur and oxygen contents in order to ensure resistance to lamellar tearing . In addition to this , it is necessary to lower the hydrogen content and reduce segregation in order to ensure the internal quality of steel . To ...
Page 267
... lower than that at both areas with sound coating and without coating , which results in lower amplitude of the reflected that is not observed as a second echo in the pattern . Therefore , three areas can be distinguished from each other ...
... lower than that at both areas with sound coating and without coating , which results in lower amplitude of the reflected that is not observed as a second echo in the pattern . Therefore , three areas can be distinguished from each other ...
Page 302
... lower riser connector collet fingers were in extremely clean condition . Some of the paint marks from manufacturing were still visible . The visually accessible portions of the tapered titanium tapered joint were clean with no apparent ...
... lower riser connector collet fingers were in extremely clean condition . Some of the paint marks from manufacturing were still visible . The visually accessible portions of the tapered titanium tapered joint were clean with no apparent ...
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
WELD METAL AND HAZ PROPERTIES | 37 |
The Effect of Intercritical Thermal Cycles on HAZ Microstructure and Toughness in CMnAlNb | 49 |
Copyright | |
17 other sections not shown
Other editions - View all
Common terms and phrases
aluminium austenite axial base metal bead behaviour brittle CGHAZ Charpy Charpy impact test chemical composition coating cooling corrosion crack front crack tip critical CTOD CTOD fracture toughness CTOD test CTOD value deformation developed distribution effect energy evaluation experimental fatigue crack ferrite Figure gauges Grade grain coarsened HAZ groove HAZ toughness heat input hydrogen cracking ICCGHAZ inherent strain intercritical kJ/mm load martensite Materials Engineering ASME measured mechanical properties method microstructure narrow gap notched panel obtained OMAE peak temperature pearlite pipe pipeline Pop-in pressure PWHT reheated residual stress samples seawater shielding gas simulation single-U Statoil steel plates steel TM1 strain gauges submerged arc welding surface notched specimen Table tempered tensile strength thermal cycle through-thickness notched TMCP steels underwater welding Volume III-A weld metal weldability welded joint welding conditions Welding Institute welding parameters welding procedure welding process welding residual stress weldment width yield strength