Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 10American Society of Mechanical Engineers, 1991 - Arctic regions |
From inside the book
Results 1-3 of 20
Page 102
... panel and its instrumentation is shown in Figure 1. A total of 30 strain gages were mounted within 100 mm gage length of each panel ( 16 of them were placed on the notched side . For the edge and back parts , the remaining 14 gages were ...
... panel and its instrumentation is shown in Figure 1. A total of 30 strain gages were mounted within 100 mm gage length of each panel ( 16 of them were placed on the notched side . For the edge and back parts , the remaining 14 gages were ...
Page 103
... panel . This local plasticity with a sudden peak was measured particularly at the front side of the panel as shown in Figure 8 . The highest strains on unnotched side , however , were observed at WM part about 45 deg from the crack ...
... panel . This local plasticity with a sudden peak was measured particularly at the front side of the panel as shown in Figure 8 . The highest strains on unnotched side , however , were observed at WM part about 45 deg from the crack ...
Page 104
... panel . The WM notched panel did not show either GSY or high crack growth resistance behaviour . Both assessment concepts are showing an agreement with respect to fracture performance of this panel . The BM notched panel has also ...
... panel . The WM notched panel did not show either GSY or high crack growth resistance behaviour . Both assessment concepts are showing an agreement with respect to fracture performance of this panel . The BM notched panel has also ...
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
WELD METAL AND HAZ PROPERTIES | 37 |
The Effect of Intercritical Thermal Cycles on HAZ Microstructure and Toughness in CMnAlNb | 49 |
Copyright | |
17 other sections not shown
Other editions - View all
Common terms and phrases
aluminium austenite axial base metal bead behaviour brittle CGHAZ Charpy Charpy impact test chemical composition coating cooling corrosion crack front crack tip critical CTOD CTOD fracture toughness CTOD test CTOD value deformation developed distribution effect energy evaluation experimental fatigue crack ferrite Figure gauges Grade grain coarsened HAZ groove HAZ toughness heat input hydrogen cracking ICCGHAZ inherent strain intercritical kJ/mm load martensite Materials Engineering ASME measured mechanical properties method microstructure narrow gap notched panel obtained OMAE peak temperature pearlite pipe pipeline Pop-in pressure PWHT reheated residual stress samples seawater shielding gas simulation single-U Statoil steel plates steel TM1 strain gauges submerged arc welding surface notched specimen Table tempered tensile strength thermal cycle through-thickness notched TMCP steels underwater welding Volume III-A weld metal weldability welded joint welding conditions Welding Institute welding parameters welding procedure welding process welding residual stress weldment width yield strength