Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 10American Society of Mechanical Engineers, 1991 - Arctic regions |
From inside the book
Results 1-3 of 51
Page 26
... possible to obtain the global strain field on a plate surface by use of optical methods . In all experimental methods , the strains measured are converted to stresses assuming elastic conditions . approximate methods : For certain ...
... possible to obtain the global strain field on a plate surface by use of optical methods . In all experimental methods , the strains measured are converted to stresses assuming elastic conditions . approximate methods : For certain ...
Page 85
... possible to include the predictive lines from the TWI scheme for avoidance of hydrogen cracking in C - Mn steels ( 9 ) . These were generated using steels with CE in the range ~ 0.40- 0.54 , and carbon contents of 0.15-0.25 % , and have ...
... possible to include the predictive lines from the TWI scheme for avoidance of hydrogen cracking in C - Mn steels ( 9 ) . These were generated using steels with CE in the range ~ 0.40- 0.54 , and carbon contents of 0.15-0.25 % , and have ...
Page 296
... possible vibrational damage . This obviously means increased work when installing Titanium systems . On all Platforms fitted out with Titanium Ballast Water Systems to date it has not been possible to utilise Titanium valves . On ...
... possible vibrational damage . This obviously means increased work when installing Titanium systems . On all Platforms fitted out with Titanium Ballast Water Systems to date it has not been possible to utilise Titanium valves . On ...
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
WELD METAL AND HAZ PROPERTIES | 37 |
The Effect of Intercritical Thermal Cycles on HAZ Microstructure and Toughness in CMnAlNb | 49 |
Copyright | |
14 other sections not shown
Other editions - View all
Common terms and phrases
alloys analysis austenite axial base metal bead behaviour brittle CGHAZ Charpy chemical composition cooling corrosion crack front crack tip critical CTOD CTOD fracture toughness CTOD test CTOD value deformation distribution effect experimental fatigue crack ferrite Figure Fracture Mechanics fusion boundary gauges grain coarsened HAZ groove HAZ region HAZ toughness heat affected zone heat input hydrogen cracking hyperbaric ICCGHAZ inherent strain intercritical kJ/mm load martensite measured mechanical properties method microstructure multi-pass welds narrow gap notched panel obtained OMAE peak temperature pearlite pipe plastic plate thickness Pop-in pressure PWHT reheated samples shielding gas simulation single-U Statoil steel plates steel TM1 strain gauges submerged arc welding surface notched specimen Table tempered tensile thermal cycle through-thickness notched titanium TMCP steel underwater welding weld metal weld passes welded joint welding conditions Welding Institute welding parameters welding procedure welding process welding residual stress weldments width yield strength