... produced in steel 1 under the conditions of thermal simulation four sets largely as expected ; the intragranular microstructure was principally ferrite with aligned second phase a rapid cool was employed in the first of except when the ...
... produced in steel 1 under the conditions of thermal simulation four sets largely as expected ; the intragranular microstructure was principally ferrite with aligned second phase a rapid cool was employed in the first of except when the ...
Page 117
... produced by the thermome- chanical control process ( TMCP ) is foresee- able . The indisputable advantage , in compa- rison with thermally treated steels , is in fact related to their lower alloying ele- ments content which imparts ...
... produced by the thermome- chanical control process ( TMCP ) is foresee- able . The indisputable advantage , in compa- rison with thermally treated steels , is in fact related to their lower alloying ele- ments content which imparts ...
Page 192
... produced . A great amount of such cameras has been produced and used in the industry particularly , in remote controlled pipe welding . 2.2.2 Black & White CCD cameras for hyperbaric welding applications The preliminary experiments with ...
... produced . A great amount of such cameras has been produced and used in the industry particularly , in remote controlled pipe welding . 2.2.2 Black & White CCD cameras for hyperbaric welding applications The preliminary experiments with ...
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
WELD METAL AND HAZ PROPERTIES | 37 |
The Effect of Intercritical Thermal Cycles on HAZ Microstructure and Toughness in CMnAlNb | 49 |
Copyright | |
17 other sections not shown
Other editions - View all
Common terms and phrases
aluminium austenite axial base metal bead behaviour brittle CGHAZ Charpy Charpy impact test chemical composition coating cooling corrosion crack front crack tip critical CTOD CTOD fracture toughness CTOD test CTOD value deformation developed distribution effect energy evaluation experimental fatigue crack ferrite Figure gauges Grade grain coarsened HAZ groove HAZ toughness heat input hydrogen cracking ICCGHAZ inherent strain intercritical kJ/mm load martensite Materials Engineering ASME measured mechanical properties method microstructure narrow gap notched panel obtained OMAE peak temperature pearlite pipe pipeline Pop-in pressure PWHT reheated residual stress samples seawater shielding gas simulation single-U Statoil steel plates steel TM1 strain gauges submerged arc welding surface notched specimen Table tempered tensile strength thermal cycle through-thickness notched TMCP steels underwater welding Volume III-A weld metal weldability welded joint welding conditions Welding Institute welding parameters welding procedure welding process welding residual stress weldment width yield strength