HT50 steel welds , T = -80 ° C A Surface notched test results ( TCGHAZ = 21 mm ) Predicted from through - thickness notched test results ( TCGHAZ = 11 mm ) A 1 0.01 0.05 0.1 0.5 1 3 0.01 0.05 0.1 0.5 3 Critical CTOD ( mm ) Critical CTOD ...
HT50 steel welds , T = -80 ° C A Surface notched test results ( TCGHAZ = 21 mm ) Predicted from through - thickness notched test results ( TCGHAZ = 11 mm ) A 1 0.01 0.05 0.1 0.5 1 3 0.01 0.05 0.1 0.5 3 Critical CTOD ( mm ) Critical CTOD ...
Page 119
STEEL Reheating Time Temp . c ) ( h ) Specimen location CVT -40 ( MPa ) ( MPa ) ( J / cm2 ) room surface 408 504 31.6 333 50 % FATT 50F temp . 1/2 th 37 ] 501 29.1 162 surface 379 485 27.9 500 4 1 B 1/2 th 356 276 301 -Surface -Mid ...
STEEL Reheating Time Temp . c ) ( h ) Specimen location CVT -40 ( MPa ) ( MPa ) ( J / cm2 ) room surface 408 504 31.6 333 50 % FATT 50F temp . 1/2 th 37 ] 501 29.1 162 surface 379 485 27.9 500 4 1 B 1/2 th 356 276 301 -Surface -Mid ...
Page 263
ULTRASONIC TESTING OF SURFACE COATINGS WITH A FOCUSSED PROBE S. Satonaka Department of Mechanical Engineering Kumamoto University Kumamoto , Japan or area areas wave theoretical analyses of polyester coated thin.
ULTRASONIC TESTING OF SURFACE COATINGS WITH A FOCUSSED PROBE S. Satonaka Department of Mechanical Engineering Kumamoto University Kumamoto , Japan or area areas wave theoretical analyses of polyester coated thin.
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
WELD METAL AND HAZ PROPERTIES | 37 |
The Effect of Intercritical Thermal Cycles on HAZ Microstructure and Toughness in CMnAlNb | 49 |
Copyright | |
13 other sections not shown
Other editions - View all
Common terms and phrases
alloys analysis application austenite axial base bead behaviour boundary calculated carbon CGHAZ changes chemical compared composition considered cooling crack crack tip critical CTOD curves cycle deformation developed direction distribution effect element energy Engineering evaluation experimental fatigue ferrite field Figure fracture toughness fusion gauges geometry Grade grain grain boundary groove hardness heat heat input higher increase initiation load lower material measured mechanical method microstructure narrow notched observed obtained offshore operation panel parameters pass performed pipe plate position possible prediction present pressure procedure produced properties range reduced regions requirements residual stress resistance samples shown shows simulation specimen steel strain strength structure surface Table temperature tempered tensile thermal thickness titanium values volume weld metal welded joint width yield zone
Bibliographic information
| Title | Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 10 |
| Contributors | OMAE Conference Committee, American Society of Mechanical Engineers. Offshore Mechanics and Arctic Engineering Division, American Society of Mechanical Engineers |
| Publisher | American Society of Mechanical Engineers, 1991 |
| Original from | the University of Michigan |
| Digitized | 4 Dec 2007 |
| ISBN | 0791807193, 9780791807194 |
| Export Citation | BiBTeX EndNote RefMan |