... oxygen the c axis expands , whilst the Cu2 - Cu2 and the Ba - Ba distances contract . Accordingly , the most ... content the dis- tance between the Cu - O planes and the Cu - O - Cu chains increases and the oxygen ( 0 , 0 , z ) apex atom ...
... oxygen the c axis expands , whilst the Cu2 - Cu2 and the Ba - Ba distances contract . Accordingly , the most ... content the dis- tance between the Cu - O planes and the Cu - O - Cu chains increases and the oxygen ( 0 , 0 , z ) apex atom ...
Page 261
... oxygen content and heat - treatment condition . Consistent with the literature lattice parameter data on pure Ti , the " a " lattice parameter of the solution - treated Ti - 8.6A1 material is relatively insensitive to the oxygen content ...
... oxygen content and heat - treatment condition . Consistent with the literature lattice parameter data on pure Ti , the " a " lattice parameter of the solution - treated Ti - 8.6A1 material is relatively insensitive to the oxygen content ...
Page 264
... Oxygen Content ( ppm ) Figure 3 : The effect of oxygen content on the " c " lattice parameter of Ti - 8.6 Al . c / a Ratio 1.6020 1.6015 Aged Condition 1.6010 1.6005 1.6000 Solution Treated Condition 1.5995 1.5990 500 1000 1500 2000 ...
... Oxygen Content ( ppm ) Figure 3 : The effect of oxygen content on the " c " lattice parameter of Ti - 8.6 Al . c / a Ratio 1.6020 1.6015 Aged Condition 1.6010 1.6005 1.6000 Solution Treated Condition 1.5995 1.5990 500 1000 1500 2000 ...
Contents
THE KINDER GENTLER PROBE OF CONDENSED MATTER | 3 |
NEUTRON SCATTERING METHODS FOR MATERIAL SCIENCE | 15 |
THE ADVANCED NEUTRON SOURCE | 27 |
Copyright | |
64 other sections not shown
Common terms and phrases
1990 Materials Research aerogel alloys analysis angle neutron scattering annealing Argonne Argonne National Laboratory atoms beam boron Bragg Bragg peaks calculated composition concentration copolymer correlation Cu-O decrease defects detector determined deuterated deuterium diffractometer diffuse scattering displacements distribution effect elastic electronic energy experimental Fermi surface ferroelastic Figure film function incoherent scattering increase inelastic interactions interface ISBN lattice parameter layers Lett magnetic Materials Research Society Materials Science measured metals method mode molecular multilayers National Laboratory neutron diffraction neutron powder diffraction neutron reflectivity Neutron Source observed obtained oxygen oxygen content particles peak phase transition phonon Phys plane polymer pore powder diffraction Proc range reactor refinement residual stresses resolution sample scattering intensity short-range order shown in Fig shows silica silicon single crystal sintering specimen spectrometer stoichiometry strain structure factor superconductivity surface Symp technique temperature thermal values Volume Vycor wafer wavelength width X-ray YBCO