Materials for Marine Systems and StructuresDennis F. Hasson, C. Robert Crowe |
From inside the book
Results 1-3 of 52
Page 150
... carbon and low alloy steels with low yield strengths ( 55 , 56 ) where both internal cracking and blistering are ... steel . In a comprehensive study of the galvanic corrosion of metals in tropical seawater , Southwell et al . ( 57 ) ...
... carbon and low alloy steels with low yield strengths ( 55 , 56 ) where both internal cracking and blistering are ... steel . In a comprehensive study of the galvanic corrosion of metals in tropical seawater , Southwell et al . ( 57 ) ...
Page 151
... steel bolts occurred where attached to more noble metal plates . On the other hand , the low alloy steel plate ... carbon steel and noble metals can reduce galvanic effects . Environmental Effects . The severity of galvanic attack of ...
... steel bolts occurred where attached to more noble metal plates . On the other hand , the low alloy steel plate ... carbon steel and noble metals can reduce galvanic effects . Environmental Effects . The severity of galvanic attack of ...
Page 251
... carbon content , 0.XX % , e.g. , 1040 steel and 4340 steels are carbon steel and Cr - Ni - Mo steels having 0.40 % carbon . The alloying elements shown in Table I are added to improve mechanical properties , forming characteristics ...
... carbon content , 0.XX % , e.g. , 1040 steel and 4340 steels are carbon steel and Cr - Ni - Mo steels having 0.40 % carbon . The alloying elements shown in Table I are added to improve mechanical properties , forming characteristics ...
Other editions - View all
Common terms and phrases
addition AISI aluminum alloys anode applications atmosphere attack Austenitic behavior bronze carbon steel cast iron cause chlorine coatings composition concentration concrete construction copper corrosion rates coupled crack crevice corrosion decrease deep dependent depth developed dissolved effect elements Engineering environment example exposed exposure factors failure fatigue Figure force fouling fracture galvanic heat important increased indicated initiation inspection joints less limited loading low alloy steels major marine materials measured mechanical metal methods North occur ocean offshore organisms oxygen Pacific performance pitting platforms presence produce properties protection reduce reference relatively reported resistance ropes salinity seawater selection ship shown solution specimens stainless steels strength Stress Corrosion Cracking structure studies surface Table temperature tests titanium treatment Type usually values wave weight weld wind zone
References to this book
Fatigue in Composites: Science and Technology of the Fatigue Response of ... Bryan Harris Limited preview - 2003 |