Page 160
... crevice corrosion of stainless steels . Most have used a multiple crevice assembly ( MCA ) which consists of 20 grooves and plateaus machined in a plastic washer type specimen ( 102 ) . Susceptibility to attack has been related to both ...
... crevice corrosion of stainless steels . Most have used a multiple crevice assembly ( MCA ) which consists of 20 grooves and plateaus machined in a plastic washer type specimen ( 102 ) . Susceptibility to attack has been related to both ...
Page 175
Dennis F. Hasson, C. Robert Crowe. tests the average crevice attack for Alloy G was 0.03 mm at 12 ° C , 0.05 mm at 28 ° C , and 0 mm at 50 ° C . In studying Alloy 825 , Hodgkiess and Rigas ( 109 ) found no crevice corrosion after 31 ...
Dennis F. Hasson, C. Robert Crowe. tests the average crevice attack for Alloy G was 0.03 mm at 12 ° C , 0.05 mm at 28 ° C , and 0 mm at 50 ° C . In studying Alloy 825 , Hodgkiess and Rigas ( 109 ) found no crevice corrosion after 31 ...
Page 304
... Crevices formed by metal - to - metal contact , metal - to - nonmetal contact , through fabricating operations such as shearing and welding , and by the attachment of fouling organisms can all result in the initiation of crevice attack ...
... Crevices formed by metal - to - metal contact , metal - to - nonmetal contact , through fabricating operations such as shearing and welding , and by the attachment of fouling organisms can all result in the initiation of crevice attack ...
Other editions - View all
Common terms and phrases
AISI aluminum alloys anode applications Austenitic Austenitic cast iron bacteria biofilm biofouling bronze C(PR carbon steel cathodic protection chemical chlorine coatings composition concentration concrete copper alloys corrosion behavior corrosion rates corrosion resistance crevice attack crevice corrosion decrease deep ocean dissolved oxygen effect Engineering erosion-corrosion exposure factors failure fatigue film fouling fracture control galvanic corrosion galvanic coupling galvanic series heat treatment high strength HSLA hydrogen immersed increased inspection intergranular intergranular corrosion ions joints loading low alloy steels macrofouling marine atmospheres marine environments marine structures Martensitic materials maximum mechanical microbial microorganisms Naval nickel North Sea occur offshore platforms Offshore Structures organisms oxidation oxygen content P(PR Pacific Ocean polluted prestressed Reinhart ropes S-N curve salinity seawater selection ship shown in Figure specimens stainless steels Stress Corrosion Cracking sulfide Table temperature tests tide zone titanium alloys Type velocity weight weld wind zinc
References to this book
Fatigue in Composites: Science and Technology of the Fatigue Response of ... Bryan Harris Limited preview - 2003 |