... EROSION - CORROSION Effect of Alloy Composition Extensive research has been done on the effect of alloying elements on the resistance of copper - base alloys ( particularly of copper - nickel alloys ) to erosion - corrosion . Freeman ...
... EROSION - CORROSION Effect of Alloy Composition Extensive research has been done on the effect of alloying elements on the resistance of copper - base alloys ( particularly of copper - nickel alloys ) to erosion - corrosion . Freeman ...
Page 220
... erosion - corrosion in aluminum brass tubes in a model condenser at Dunkerque . The difference in performance of aluminum brass at the two locations may be the result of the difference in operating conditions on the quality of seawater ...
... erosion - corrosion in aluminum brass tubes in a model condenser at Dunkerque . The difference in performance of aluminum brass at the two locations may be the result of the difference in operating conditions on the quality of seawater ...
Page 222
... erosion - corrosion of tubes can be avoided . Effect of Temperature Data compiled from several studies on the erosion - corrosion of copper- base alloys at different temperatures show a mixed trend with regard to the effect of ...
... erosion - corrosion of tubes can be avoided . Effect of Temperature Data compiled from several studies on the erosion - corrosion of copper- base alloys at different temperatures show a mixed trend with regard to the effect of ...
Other editions - View all
Common terms and phrases
AISI aluminum alloys anode applications Austenitic Austenitic cast iron bacteria biofilm biofouling bronze C(PR carbon steel cathodic protection chemical chlorine coatings composition concentration concrete copper alloys corrosion behavior corrosion rates corrosion resistance crevice attack crevice corrosion decrease deep ocean dissolved oxygen effect Engineering erosion-corrosion exposure factors failure fatigue film fouling fracture control galvanic corrosion galvanic coupling galvanic series heat treatment high strength HSLA hydrogen immersed increased inspection intergranular intergranular corrosion ions joints loading low alloy steels macrofouling marine atmospheres marine environments marine structures Martensitic materials maximum mechanical microbial microorganisms Naval nickel North Sea occur offshore platforms Offshore Structures organisms oxidation oxygen content P(PR Pacific Ocean polluted prestressed Reinhart ropes S-N curve salinity seawater selection ship shown in Figure specimens stainless steels Stress Corrosion Cracking sulfide Table temperature tests tide zone titanium alloys Type velocity weight weld wind zinc
References to this book
Fatigue in Composites: Science and Technology of the Fatigue Response of ... Bryan Harris Limited preview - 2003 |