Page 218
... sulfide concentration , seawater velocity , and duration of sulfide exposure on corro- sion of Cu - 10Ni and Cu - 30Ni . All exposures were conducted in fresh seawater , with the sulfide concentration varying from 0.007 to 0.25 mg / l ...
... sulfide concentration , seawater velocity , and duration of sulfide exposure on corro- sion of Cu - 10Ni and Cu - 30Ni . All exposures were conducted in fresh seawater , with the sulfide concentration varying from 0.007 to 0.25 mg / l ...
Page 219
... sulfide . These results also indicated that where sulfide exposure conditions were sufficient to initiate attack , the seawater velocity dependence was minimal over the range of 0.5 to 5.3 m / s . A number of researchers have ...
... sulfide . These results also indicated that where sulfide exposure conditions were sufficient to initiate attack , the seawater velocity dependence was minimal over the range of 0.5 to 5.3 m / s . A number of researchers have ...
Page 232
... Sulfide Modified Seawater . " Journal of Testing and Evaluation JTEVA 8 ( 2 ) , 74–79 . 108. Deverell , H. E. , and Davis , J. A. ( 1978 ) . “ Effect of Sulfides and Other Pollutants on the Seawater Corrosion of Stainless Steels and ...
... Sulfide Modified Seawater . " Journal of Testing and Evaluation JTEVA 8 ( 2 ) , 74–79 . 108. Deverell , H. E. , and Davis , J. A. ( 1978 ) . “ Effect of Sulfides and Other Pollutants on the Seawater Corrosion of Stainless Steels and ...
Other editions - View all
Common terms and phrases
AISI aluminum alloys anode applications Austenitic Austenitic cast iron bacteria biofilm biofouling bronze C(PR carbon steel cathodic protection chemical chlorine coatings composition concentration concrete copper alloys corrosion behavior corrosion rates corrosion resistance crevice attack crevice corrosion decrease deep ocean dissolved oxygen effect Engineering erosion-corrosion exposure factors failure fatigue film fouling fracture control galvanic corrosion galvanic coupling galvanic series heat treatment high strength HSLA hydrogen immersed increased inspection intergranular intergranular corrosion ions joints loading low alloy steels macrofouling marine atmospheres marine environments marine structures Martensitic materials maximum mechanical microbial microorganisms Naval nickel North Sea occur offshore platforms Offshore Structures organisms oxidation oxygen content P(PR Pacific Ocean polluted prestressed Reinhart ropes S-N curve salinity seawater selection ship shown in Figure specimens stainless steels Stress Corrosion Cracking sulfide Table temperature tests tide zone titanium alloys Type velocity weight weld wind zinc
References to this book
Fatigue in Composites: Science and Technology of the Fatigue Response of ... Bryan Harris Limited preview - 2003 |